AA Standards Grade 5052 O

Want to keep this datasheet? Save it now in your required format

Ashby charts

See where AA Standards Grade 5052 O falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.68 - 2.7 g/cm³ at 20 °C

Dimension

Dimensions

Dicke

Mechanical

Elastic modulus

E

70 GPa at 20 °C

Elongation

A

46 % at -195 °C

Elongation in 50 mm

Hide chart

Elongation A100

A100

16 - 27 % at 20 °C

Elongation A50

A50

13 - 25 % at 20 °C

Fatigue strength

SNf

110 MPa at 20 °C

for 5x10⁸ cycles

Hardness, Brinell

HB

47 [-] at 20 °C

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Typical for Wrought 5000 Series Aluminium

Shear modulus

G

25.9 GPa at 20 °C

Shear strength

τ

125 MPa at 20 °C

Tensile strength

Rm

303 MPa at -195 °C

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Unlock all property charts

Create your account on Matmatch to view all property charts and access other premium features for free.

Sign in

Yield strength

YS

80 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

110 MPa at -196 °C

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Unlock all property charts

Create your account on Matmatch to view all property charts and access other premium features for free.

Sign in

Thermal

Coefficient of thermal expansion

α

2.38E-5 - 2.4E-5 1/K at 20 °C

Unlock all property charts

Create your account on Matmatch to view all property charts and access other premium features for free.

Sign in

Max service temperature

Tmax

150 °C

Typical for Wrought 5000 Series Aluminium

Melting point

Tm

605 - 650 °C

Specific heat capacity

cp

900 J/(kg·K) at 20 °C

Thermal conductivity

λ

138 - 140 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

2.00E+7 - 2.03E+8 S/m at 20 °C

Unstated/Typical value,Typical/derived value

Electrical resistivity

ρel

5E-8 Ω·m at 20 °C

Specific Electrical conductivity

35 % IACS

Unstated value,Typical value

Chemical properties

Element

Weight %

Comment

Al

95.8 - 97.7 %

Mg

2.2 - 2.8 %

Cr

0.15 - 0.35 %

Cu

0 - 0.1 %

Fe

0 - 0.4 %

More

Technological properties

Brazing

general: limited brazing

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O, H32), sufficient (H34, H36, H38)

Workability

general (condition): good (O), acceptable (H32, H34), poor(H36, H38)

This material data has been provided by MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials,AluKey.