AA Standards Grade 5056 H18

View suppliers (9)
Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.64 g/cm³

Show Material materials with Density of 2.64 g/cm³

H18

AA Standards, ASTM B211

2.64 g/cm³

Show Material materials with Density of 2.64 g/cm³

H18

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

H18

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Bending Fatigue Strength

150.0 MPa

Show Material materials with Bending Fatigue Strength of 150.0 MPa

H18

AA Standards

Elastic modulus

71.0 GPa

Show Material materials with Elastic modulus of 71.0 GPa

H18

AA Standards, ASTM B211

71 GPa

Show Material materials with Elastic modulus of 71 GPa

H18

Elongation

9.0 %

Show Material materials with Elongation of 9.0 %

H18

AA Standards

A100

9.7 %

Show Material materials with Elongation of 9.7 %

H18

24 °C

15 %

Show Material materials with Elongation of 15 %

H18

Elongation in 50 mm

149 °C

30 %

Show Material materials with Elongation of 30 %

H18

Elongation in 50 mm

204 °C

50 %

Show Material materials with Elongation of 50 %

H18

Elongation in 50 mm

260 °C

80 %

Show Material materials with Elongation of 80 %

H18

Elongation in 50 mm

316 °C

100 %

Show Material materials with Elongation of 100 %

H18

Elongation in 50 mm

Fatigue strength

152 MPa

Show Material materials with Fatigue strength of 152 MPa

H18

for 5x10⁸ cycles

Hardness, Brinell

105.0 [-]

Show Material materials with Hardness, Brinell of 105.0 [-]

H18

AA Standards

105.0 [-]

Show Material materials with Hardness, Brinell of 105.0 [-]

H18

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

25.9 GPa

Show Material materials with Shear modulus of 25.9 GPa

H18

Shear strength

234.0 MPa

Show Material materials with Shear strength of 234.0 MPa

H18

Tensile strength

400.0 MPa

Show Material materials with Tensile strength of 400.0 MPa

H18

AA Standards, ASTM B211

435.0 MPa

Show Material materials with Tensile strength of 435.0 MPa

H18

AA Standards

440.0 MPa

Show Material materials with Tensile strength of 440.0 MPa

H18

24 °C

414 MPa

Show Material materials with Tensile strength of 414 MPa

H18

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

149 °C

262 MPa

Show Material materials with Tensile strength of 262 MPa

H18

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

204 °C

179 MPa

Show Material materials with Tensile strength of 179 MPa

H18

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

110 MPa

Show Material materials with Tensile strength of 110 MPa

H18

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

316 °C

76 MPa

Show Material materials with Tensile strength of 76 MPa

H18

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Yield strength

405.0 MPa

Show Material materials with Yield strength of 405.0 MPa

H18

AA Standards

RP02

410.0 MPa

Show Material materials with Yield strength of 410.0 MPa

H18

24 °C

345 MPa

Show Material materials with Yield strength of 345 MPa

H18

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

149 °C

214 MPa

Show Material materials with Yield strength of 214 MPa

H18

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

204 °C

124 MPa

Show Material materials with Yield strength of 124 MPa

H18

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

260 °C

69 MPa

Show Material materials with Yield strength of 69 MPa

H18

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

316 °C

48 MPa

Show Material materials with Yield strength of 48 MPa

H18

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

H18

20 °C

2.41e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.41e-05 1/K

H18

AA Standards, ASTM B211

100 °C

2.41e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.41e-05 1/K

H18

AA Standards, ASTM B211

Max service temperature

150.0 °C

Show Material materials with Max service temperature of 150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

565.0 - 640.0 °C

Show Material materials with Melting point of 565.0 - 640.0 °C

H18

AA Standards, ASTM B211

570.0 °C

Show Material materials with Melting point of 570.0 °C

H18

Specific heat capacity

910.0 J/(kg·K)

Show Material materials with Specific heat capacity of 910.0 J/(kg·K)

H18

Thermal conductivity

109.0 - 117.0 W/(m·K)

Show Material materials with Thermal conductivity of 109.0 - 117.0 W/(m·K)

H18

AA Standards, ASTM B211

Electrical

PropertyValueConditionRelated Standards

Electrical conductivity

16000000.0 - 17000000.0 S/m

Show Material materials with Electrical conductivity of 16000000.0 - 17000000.0 S/m

H18

AA Standards, ASTM B211

Electrical resistivity

5.88e-08 - 6.25e-08 Ω·m

Show Material materials with Electrical resistivity of 5.88e-08 - 6.25e-08 Ω·m

H18

AA Standards, ASTM B211

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

93.0 - 95.4 %

Show Material materials with Aluminium of 93.0 - 95.4 %

H18

Chromium

0.05 - 0.2 %

Show Material materials with Chromium of 0.05 - 0.2 %

H18

AA Standards, ASTM B211

Copper

0.1 %

Show Material materials with Copper of 0.1 %

H18

AA Standards, ASTM B211

Iron

0.40 %

Show Material materials with Iron of 0.40 %

H18

AA Standards, ASTM B211

0.4 %

Show Material materials with Iron of 0.4 %

H18

Magnesium

4.5 - 5.6 %

Show Material materials with Magnesium of 4.5 - 5.6 %

H18

AA Standards, ASTM B211

Manganese

0.05 - 0.2 %

Show Material materials with Manganese of 0.05 - 0.2 %

H18

AA Standards, ASTM B211

Other

0.15 %

Show Material materials with Other of 0.15 %

H18

Silicon

0.3 %

Show Material materials with Silicon of 0.3 %

H18

AA Standards, ASTM B211

Zinc

0.1 %

Show Material materials with Zinc of 0.1 %

H18

AA Standards, ASTM B211

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (O, H111, H12, H32, H14, H34), c (H18, H38), d (H192, H392), general: sehr gut, ohne Schutz in industrieller oder Seewasser-Atmosphäre (O, H111, H12, H32, H14, H34, H18, H38), b (H192, H392)

General machinability

General: poor (O, H111, H12, H32), sufficient (H14, H34, H18, H38), good to acceptable (H192, H392)

Workability

general (condition): good (O, H111), acceptable (H12, H32, H14, H34), poor(H18, H38), d (H192, H392)