Properties
General
| Property | Value | Condition |
|---|---|---|
Density | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | H111 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 71.0 GPa Show Material materials with Elastic modulus of 71.0 GPa | H111 | ||
Elongation | 10.0 % Show Material materials with Elongation of 10.0 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 | A100 |
12.0 % Show Material materials with Elongation of 12.0 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 | A50 | |
12.0 % Show Material materials with Elongation of 12.0 % | H111 | AA Standards, ASTM B247 | A100 | |
13.0 % Show Material materials with Elongation of 13.0 % | H111 | |||
14.0 % Show Material materials with Elongation of 14.0 % | H111 | AA Standards, ASTM B247 | A50 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 270.0 MPa Show Material materials with Tensile strength of 270.0 MPa | H111 | AA Standards, ASTM B247 | |
275.0 MPa Show Material materials with Tensile strength of 275.0 MPa | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | ||
290.0 MPa Show Material materials with Tensile strength of 290.0 MPa | H111 | AA Standards, ASTM B247 | ||
310.0 MPa Show Material materials with Tensile strength of 310.0 MPa | H111 | |||
Yield strength | 110.0 MPa Show Material materials with Yield strength of 110.0 MPa | H111 | AA Standards, ASTM B247 | RP02 |
140.0 MPa Show Material materials with Yield strength of 140.0 MPa | H111 | AA Standards, ASTM B247 | RP02 | |
150.0 MPa Show Material materials with Yield strength of 150.0 MPa | H111 | AA Standards, ASTM B247 | RP02 | |
150.0 MPa Show Material materials with Yield strength of 150.0 MPa | H111 | |||
165.0 MPa Show Material materials with Yield strength of 165.0 MPa | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | RP02 |
Thermal
| Property | Value | Condition | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H111 | |
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |
Melting point | 580.0 °C Show Material materials with Melting point of 580.0 °C | H111 | |
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | H111 | |
Thermal conductivity | 120.0 W/(m·K) Show Material materials with Thermal conductivity of 120.0 W/(m·K) | H111 |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 31000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m Show Material materials with Electrical resistivity of 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 92.4 - 95.6 % Show Material materials with Aluminium of 92.4 - 95.6 % | H111 | |
Chromium | 0.05 - 0.25 % Show Material materials with Chromium of 0.05 - 0.25 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Iron | 0.40 % Show Material materials with Iron of 0.40 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
0.4 % Show Material materials with Iron of 0.4 % | H111 | ||
Magnesium | 4.0 - 4.9 % Show Material materials with Magnesium of 4.0 - 4.9 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Manganese | 0.4 - 1.0 % Show Material materials with Manganese of 0.4 - 1.0 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H111 | |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: kein Schadensfall im Betrieb und bei Labortests (O, H321, H116), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (H111), general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor | |
| Workability | general (condition): acceptable (O), poor(H321, H116, H111) | |