AA Standards Grade 5083 H112

Want to keep this datasheet? Save it now in your required format

Description

Related Standards

Equivalent Materials

Ashby charts

See where AA Standards Grade 5083 H112 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.7 g/cm³ at 20 °C

Dimension

Dimensions

Wanddicke

Mechanical

Elastic modulus

E

71 GPa at 20 °C

Elongation

A

13 % at 20 °C

Elongation A100

A100

10 - 14 % at 20 °C

Elongation A50

A50

12 - 16 % at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Typical for Wrought 5000 Series Aluminium

Shear modulus

G

26 - 26.5 GPa at 20 °C

Typical for Wrought 5000 Series Aluminium

Tensile strength

Rm

270 - 310 MPa at 20 °C

Yield strength

YS

130 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

110 - 140 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.4E-5 1/K at 20 °C

Max service temperature

Tmax

150 °C

Typical for Wrought 5000 Series Aluminium

Melting point

Tm

580 °C

Specific heat capacity

cp

900 J/(kg·K) at 20 °C

Thermal conductivity

λ

120 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

1.68E+8 S/m at 20 °C

Electrical resistivity

ρel

3.3E-8 - 5E-8 Ω·m at 20 °C

Typical for Wrought 5000 Series Aluminium

Chemical properties

Element

Weight %

Comment

Al

92.4 - 95.6 %

Mg

4 - 4.9 %

Mn

0.4 - 1 %

Cr

0.05 - 0.25 %

Cu

0 - 0.1 %

More

Technological properties

Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: kein Schadensfall im Betrieb und bei Labortests (O, H321, H116), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (H111), general: very good, without protection in industrial or seawater atmosphere

General machinability

General: poor

Workability

general (condition): acceptable (O), poor(H321, H116, H111)

This material data has been provided by MakeItFrom.com,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.