Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.66 g/cm³ Show Material materials with Density of 2.66 g/cm³ | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
2.66 g/cm³ Show Material materials with Density of 2.66 g/cm³ | H34 | ||
2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | H34 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 130.0 MPa Show Material materials with Bending Fatigue Strength of 130.0 MPa | H34 | AA Standards | |
Compressive modulus | 70.7 MPa Show Material materials with Compressive modulus of 70.7 MPa | H34 | ||
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | |
70 GPa Show Material materials with Elastic modulus of 70 GPa | H34 | |||
Elongation | 4.0 % Show Material materials with Elongation of 4.0 % | H34 | AA Standards, ASTM B209 | A50 |
4.0 % Show Material materials with Elongation of 4.0 % | H34 | AA Standards, ASTM B210 | A100 | |
5.0 % Show Material materials with Elongation of 5.0 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313 | A50 | |
6.0 % Show Material materials with Elongation of 6.0 % | H34 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | |
8.8 % Show Material materials with Elongation of 8.8 % | H34 | |||
9.0 % Show Material materials with Elongation of 9.0 % | H34 | AA Standards, ASTM B209 | A100 | |
10.0 % Show Material materials with Elongation of 10.0 % | H34 | AA Standards, ASTM B209, ASTM B547 | A50 | |
13.0 % Show Material materials with Elongation of 13.0 % | H34 | AA Standards | A50 | |
13 % Show Material materials with Elongation of 13 % | H34 | |||
Fatigue strength | 131 MPa Show Material materials with Fatigue strength of 131 MPa | H34 | for 5x10⁸ cycles | |
Hardness, Brinell | 73.0 [-] Show Material materials with Hardness, Brinell of 73.0 [-] | H34 | AA Standards | |
73.0 [-] Show Material materials with Hardness, Brinell of 73.0 [-] | H34 | 500 kg load, 10 mm ball | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 25.9 GPa Show Material materials with Shear modulus of 25.9 GPa | H34 | ||
Shear strength | 166.0 MPa Show Material materials with Shear strength of 166.0 MPa | H34 | ||
Tensile strength | 270.0 - 320.0 MPa Show Material materials with Tensile strength of 270.0 - 320.0 MPa | H34 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
270.0 MPa Show Material materials with Tensile strength of 270.0 MPa | H34 | AA Standards, ASTM B210, ASTM B211 | ||
290.0 MPa Show Material materials with Tensile strength of 290.0 MPa | H34 | AA Standards | ||
290 MPa Show Material materials with Tensile strength of 290 MPa | H34 | |||
300.0 MPa Show Material materials with Tensile strength of 300.0 MPa | H34 | |||
Yield strength | 200.0 MPa Show Material materials with Yield strength of 200.0 MPa | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 | RP02 |
230.0 MPa Show Material materials with Yield strength of 230.0 MPa | H34 | AA Standards | RP02 | |
230 MPa Show Material materials with Yield strength of 230 MPa | H34 | RP02 | ||
230.0 MPa Show Material materials with Yield strength of 230.0 MPa | H34 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H34 | |||
20 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | ||
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 590.0 - 645.0 °C Show Material materials with Melting point of 590.0 - 645.0 °C | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | ||
590.0 °C Show Material materials with Melting point of 590.0 °C | H34 | ||||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | H34 | |||
Thermal conductivity | 126 W/(m·K) Show Material materials with Thermal conductivity of 126 W/(m·K) | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | ||
130.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 W/(m·K) | H34 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 19000000.0 S/m Show Material materials with Electrical conductivity of 19000000.0 S/m | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Electrical resistivity | 5.26e-08 Ω·m Show Material materials with Electrical resistivity of 5.26e-08 Ω·m | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 94.4 - 96.8 % Show Material materials with Aluminium of 94.4 - 96.8 % | H34 | |
Chromium | 0.15 - 0.35 % Show Material materials with Chromium of 0.15 - 0.35 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Iron | 0.40 % Show Material materials with Iron of 0.40 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
0.4 % Show Material materials with Iron of 0.4 % | H34 | ||
Magnesium | 3.1 - 3.9 % Show Material materials with Magnesium of 3.1 - 3.9 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H34 | |
Silicon | 0.25 % Show Material materials with Silicon of 0.25 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Titanium | 0.2 % Show Material materials with Titanium of 0.2 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Zinc | 0.2 % Show Material materials with Zinc of 0.2 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |