General
Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.66 g/cm³ Show Material materials with Density of 2.66 g/cm³ | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
2.66 g/cm³ Show Material materials with Density of 2.66 g/cm³ | H36 | ||
2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | H36 |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Bending Fatigue Strength | 140.0 MPa Show Material materials with Bending Fatigue Strength of 140.0 MPa | H36 | AA Standards | |
Compressive modulus | 70.7 MPa Show Material materials with Compressive modulus of 70.7 MPa | H36 | ||
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | |
70 GPa Show Material materials with Elastic modulus of 70 GPa | H36 | |||
Elongation | 3.0 % Show Material materials with Elongation of 3.0 % | H36 | AA Standards, ASTM B209 | A50 |
4.0 % Show Material materials with Elongation of 4.0 % | H36 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | |
9.2 % Show Material materials with Elongation of 9.2 % | H36 | |||
12.0 % Show Material materials with Elongation of 12.0 % | H36 | AA Standards | A50 | |
12 % Show Material materials with Elongation of 12 % | H36 | |||
Fatigue strength | 138 MPa Show Material materials with Fatigue strength of 138 MPa | H36 | for 5x10⁸ cycles | |
Hardness, Brinell | 78.0 [-] Show Material materials with Hardness, Brinell of 78.0 [-] | H36 | AA Standards | |
78.0 [-] Show Material materials with Hardness, Brinell of 78.0 [-] | H36 | 500 kg load, 10 mm ball | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 25.9 GPa Show Material materials with Shear modulus of 25.9 GPa | H36 | ||
Shear strength | 179.0 MPa Show Material materials with Shear strength of 179.0 MPa | H36 | ||
Tensile strength | 290.0 - 340.0 MPa Show Material materials with Tensile strength of 290.0 - 340.0 MPa | H36 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
290.0 MPa Show Material materials with Tensile strength of 290.0 MPa | H36 | AA Standards, ASTM B211 | ||
310.0 MPa Show Material materials with Tensile strength of 310.0 MPa | H36 | AA Standards, ASTM B210 | ||
310 MPa Show Material materials with Tensile strength of 310 MPa | H36 | |||
Yield strength | 220.0 MPa Show Material materials with Yield strength of 220.0 MPa | H36 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | RP02 |
235.0 MPa Show Material materials with Yield strength of 235.0 MPa | H36 | AA Standards, ASTM B210 | RP02 | |
250.0 MPa Show Material materials with Yield strength of 250.0 MPa | H36 | AA Standards | RP02 | |
250 MPa Show Material materials with Yield strength of 250 MPa | H36 | RP02 | ||
250.0 MPa Show Material materials with Yield strength of 250.0 MPa | H36 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H36 | |||
20 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | ||
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 590.0 - 645.0 °C Show Material materials with Melting point of 590.0 - 645.0 °C | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | ||
590.0 °C Show Material materials with Melting point of 590.0 °C | H36 | ||||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | H36 | |||
Thermal conductivity | 126 W/(m·K) Show Material materials with Thermal conductivity of 126 W/(m·K) | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | ||
130.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 W/(m·K) | H36 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 19000000.0 S/m Show Material materials with Electrical conductivity of 19000000.0 S/m | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Electrical resistivity | 5.26e-08 Ω·m Show Material materials with Electrical resistivity of 5.26e-08 Ω·m | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 94.4 - 96.8 % Show Material materials with Aluminium of 94.4 - 96.8 % | H36 | |
Chromium | 0.15 - 0.35 % Show Material materials with Chromium of 0.15 - 0.35 % | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Iron | 0.40 % Show Material materials with Iron of 0.40 % | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
0.4 % Show Material materials with Iron of 0.4 % | H36 | ||
Magnesium | 3.1 - 3.9 % Show Material materials with Magnesium of 3.1 - 3.9 % | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H36 | |
Silicon | 0.25 % Show Material materials with Silicon of 0.25 % | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Titanium | 0.2 % Show Material materials with Titanium of 0.2 % | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Zinc | 0.2 % Show Material materials with Zinc of 0.2 % | H36 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
Technological properties
Property | ||
---|---|---|
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) |