AA Standards Grade 5154 O

View suppliers (4)
Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.66 g/cm³

Show Material materials with Density of 2.66 g/cm³

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

2.66 g/cm³

Show Material materials with Density of 2.66 g/cm³

O

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

O

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Bending Fatigue Strength

115.0 MPa

Show Material materials with Bending Fatigue Strength of 115.0 MPa

O

AA Standards

Compressive modulus

70.7 MPa

Show Material materials with Compressive modulus of 70.7 MPa

O

Elastic modulus

70.0 GPa

Show Material materials with Elastic modulus of 70.0 GPa

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

70 GPa

Show Material materials with Elastic modulus of 70 GPa

O

Elongation

-195 °C

46 %

Show Material materials with Elongation of 46 %

O

Elongation in 50 mm

-80 °C

35 %

Show Material materials with Elongation of 35 %

O

Elongation in 50 mm

9.0 %

Show Material materials with Elongation of 9.0 %

O

AA Standards, ASTM B210

A100

10.0 %

Show Material materials with Elongation of 10.0 %

O

AA Standards, ASTM B210

A50

12.0 %

Show Material materials with Elongation of 12.0 %

O

AA Standards, ASTM B209

A50

13.0 %

Show Material materials with Elongation of 13.0 %

O

AA Standards, ASTM B209, ASTM B313

A50

16.0 %

Show Material materials with Elongation of 16.0 %

O

AA Standards, ASTM B209, ASTM B313, ASTM B547

A50

16.0 %

Show Material materials with Elongation of 16.0 %

O

AA Standards, ASTM B209

A100

18.0 %

Show Material materials with Elongation of 18.0 %

O

AA Standards, ASTM B209, ASTM B547

A50

21.0 %

Show Material materials with Elongation of 21.0 %

O

22.0 %

Show Material materials with Elongation of 22.0 %

O

AA Standards, ASTM B211

A100

25.0 %

Show Material materials with Elongation of 25.0 %

O

AA Standards, ASTM B211

A50

27.0 %

Show Material materials with Elongation of 27.0 %

O

AA Standards

A50

0 °C

32 %

Show Material materials with Elongation of 32 %

O

Elongation in 50 mm

24 °C

30 %

Show Material materials with Elongation of 30 %

O

Elongation in 50 mm

100 °C

36 %

Show Material materials with Elongation of 36 %

O

Elongation in 50 mm

150 °C

50 %

Show Material materials with Elongation of 50 %

O

Elongation in 50 mm

205 °C

60 %

Show Material materials with Elongation of 60 %

O

Elongation in 50 mm

260 °C

80 %

Show Material materials with Elongation of 80 %

O

Elongation in 50 mm

315 °C

110 %

Show Material materials with Elongation of 110 %

O

Elongation in 50 mm

370 °C

130 %

Show Material materials with Elongation of 130 %

O

Elongation in 50 mm

Fatigue strength

117 MPa

Show Material materials with Fatigue strength of 117 MPa

O

for 5x10⁸ cycles

Hardness, Brinell

58.0 [-]

Show Material materials with Hardness, Brinell of 58.0 [-]

O

AA Standards

58.0 [-]

Show Material materials with Hardness, Brinell of 58.0 [-]

O

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

25.9 GPa

Show Material materials with Shear modulus of 25.9 GPa

O

Shear strength

152.0 MPa

Show Material materials with Shear strength of 152.0 MPa

O

Tensile strength

-195 °C

360 MPa

Show Material materials with Tensile strength of 360 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

248 MPa

Show Material materials with Tensile strength of 248 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205.0 - 285.0 MPa

Show Material materials with Tensile strength of 205.0 - 285.0 MPa

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

240.0 MPa

Show Material materials with Tensile strength of 240.0 MPa

O

AA Standards

0 °C

240 MPa

Show Material materials with Tensile strength of 240 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

24 °C

240 MPa

Show Material materials with Tensile strength of 240 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

240 MPa

Show Material materials with Tensile strength of 240 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

200 MPa

Show Material materials with Tensile strength of 200 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

152 MPa

Show Material materials with Tensile strength of 152 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

117 MPa

Show Material materials with Tensile strength of 117 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

75 MPa

Show Material materials with Tensile strength of 75 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

370 °C

40 MPa

Show Material materials with Tensile strength of 40 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Yield strength

-196 °C

130 MPa

Show Material materials with Yield strength of 130 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-80 °C

115 MPa

Show Material materials with Yield strength of 115 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-28 °C

115 MPa

Show Material materials with Yield strength of 115 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

75.0 MPa

Show Material materials with Yield strength of 75.0 MPa

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

RP02

94.0 MPa

Show Material materials with Yield strength of 94.0 MPa

O

115.0 MPa

Show Material materials with Yield strength of 115.0 MPa

O

AA Standards

RP02

24 °C

115 MPa

Show Material materials with Yield strength of 115 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

100 °C

115 MPa

Show Material materials with Yield strength of 115 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

149 °C

110 MPa

Show Material materials with Yield strength of 110 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

204 °C

105 MPa

Show Material materials with Yield strength of 105 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

260 °C

75 MPa

Show Material materials with Yield strength of 75 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

316 °C

50 MPa

Show Material materials with Yield strength of 50 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

317 °C

29 MPa

Show Material materials with Yield strength of 29 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

O

20 °C

2.3899999999999998e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

100 °C

2.3899999999999998e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

Max service temperature

150.0 °C

Show Material materials with Max service temperature of 150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

590.0 - 645.0 °C

Show Material materials with Melting point of 590.0 - 645.0 °C

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

590.0 °C

Show Material materials with Melting point of 590.0 °C

O

Specific heat capacity

900.0 J/(kg·K)

Show Material materials with Specific heat capacity of 900.0 J/(kg·K)

O

Thermal conductivity

126 W/(m·K)

Show Material materials with Thermal conductivity of 126 W/(m·K)

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

130.0 W/(m·K)

Show Material materials with Thermal conductivity of 130.0 W/(m·K)

O

Electrical

PropertyValueConditionRelated Standards

Electrical conductivity

19000000.0 S/m

Show Material materials with Electrical conductivity of 19000000.0 S/m

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

Electrical resistivity

5.26e-08 Ω·m

Show Material materials with Electrical resistivity of 5.26e-08 Ω·m

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

94.4 - 96.8 %

Show Material materials with Aluminium of 94.4 - 96.8 %

O

Chromium

0.15 - 0.35 %

Show Material materials with Chromium of 0.15 - 0.35 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

Copper

0.1 %

Show Material materials with Copper of 0.1 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

Iron

0.40 %

Show Material materials with Iron of 0.40 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

0.4 %

Show Material materials with Iron of 0.4 %

O

Magnesium

3.1 - 3.9 %

Show Material materials with Magnesium of 3.1 - 3.9 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

Manganese

0.1 %

Show Material materials with Manganese of 0.1 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

Other

0.15 %

Show Material materials with Other of 0.15 %

O

Silicon

0.25 %

Show Material materials with Silicon of 0.25 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

Titanium

0.2 %

Show Material materials with Titanium of 0.2 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

Zinc

0.2 %

Show Material materials with Zinc of 0.2 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O, H32), sufficient (H34, H36, H38)

Workability

general (condition): good (O), acceptable (H32, H34), poor(H36, H38)