Properties
General
| Property | Value | Condition |
|---|---|---|
Density | 2.69 g/cm³ Show Material materials with Density of 2.69 g/cm³ | H112 |
2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | H112 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Compressive modulus | 71.0 MPa Show Material materials with Compressive modulus of 71.0 MPa | H112 | ||
Elastic modulus | 70 GPa Show Material materials with Elastic modulus of 70 GPa | H112 | ||
71.0 GPa Show Material materials with Elastic modulus of 71.0 GPa | H112 | |||
Elongation | 8.0 % Show Material materials with Elongation of 8.0 % | H112 | AA Standards, ASTM B209, ASTM B547 | A50 |
9.0 % Show Material materials with Elongation of 9.0 % | H112 | AA Standards, ASTM B209 | A100 | |
10.0 % Show Material materials with Elongation of 10.0 % | H112 | AA Standards, ASTM B221, ASTM B241 | A100 | |
12.0 % Show Material materials with Elongation of 12.0 % | H112 | AA Standards, ASTM B221, ASTM B241 | A50 | |
13.0 % Show Material materials with Elongation of 13.0 % | H112 | AA Standards, ASTM B209 | A100 | |
14.0 % Show Material materials with Elongation of 14.0 % | H112 | |||
18.0 % Show Material materials with Elongation of 18.0 % | H112 | AA Standards | A50 | |
18 % Show Material materials with Elongation of 18 % | H112 | |||
Hardness, Brinell | 62.0 [-] Show Material materials with Hardness, Brinell of 62.0 [-] | H112 | AA Standards | |
62.0 [-] Show Material materials with Hardness, Brinell of 62.0 [-] | H112 | 500 kg load, 10 mm ball | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Shear strength | 159.0 MPa Show Material materials with Shear strength of 159.0 MPa | H112 | ||
Tensile strength | 215.0 MPa Show Material materials with Tensile strength of 215.0 MPa | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
220.0 MPa Show Material materials with Tensile strength of 220.0 MPa | H112 | AA Standards, ASTM B209, ASTM B547 | ||
250.0 MPa Show Material materials with Tensile strength of 250.0 MPa | H112 | AA Standards | ||
250 MPa Show Material materials with Tensile strength of 250 MPa | H112 | |||
Yield strength | 85.0 MPa Show Material materials with Yield strength of 85.0 MPa | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | RP02 |
110.0 MPa Show Material materials with Yield strength of 110.0 MPa | H112 | |||
125.0 MPa Show Material materials with Yield strength of 125.0 MPa | H112 | AA Standards, ASTM B209, ASTM B547 | RP02 | |
125 MPa Show Material materials with Yield strength of 125 MPa | H112 | RP02 |
Thermal
| Property | Value | Condition | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H112 | |
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |
Melting point | 600.0 °C Show Material materials with Melting point of 600.0 °C | H112 | |
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | H112 | |
Thermal conductivity | 130.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 W/(m·K) | H112 |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 31000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m Show Material materials with Electrical resistivity of 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 94.5 - 97.1 % Show Material materials with Aluminium of 94.5 - 97.1 % | H112 | |
Chromium | 0.05 - 0.2 % Show Material materials with Chromium of 0.05 - 0.2 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Iron | 0.40 % Show Material materials with Iron of 0.40 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
0.4 % Show Material materials with Iron of 0.4 % | H112 | ||
Magnesium | 2.4 - 3.0 % Show Material materials with Magnesium of 2.4 - 3.0 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Manganese | 0.5 - 1.0 % Show Material materials with Manganese of 0.5 - 1.0 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H112 | |
Silicon | 0.25 % Show Material materials with Silicon of 0.25 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Titanium | 0.2 % Show Material materials with Titanium of 0.2 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32, H111), sufficient (H34) | |
| Workability | general (condition): good (O), acceptable (H32, H34, H111) | |