Mechanical
Property | Value | Condition | Comment |
---|---|---|---|
Compressive modulus | 69.6 MPa Show Material materials with Compressive modulus of 69.6 MPa | T4 | |
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | T4 | |
Elongation | 17.0 % Show Material materials with Elongation of 17.0 % | T4 | |
Fatigue strength | 97 MPa Show Material materials with Fatigue strength of 97 MPa | T4 | Min., for 5x10⁸ cycles |
Hardness, Rockwell Superficial 15-T | 70.0 [-] Show Material materials with Hardness, Rockwell Superficial 15-T of 70.0 [-] | T4 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | |
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | |
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | |
Shear strength | 152.0 MPa Show Material materials with Shear strength of 152.0 MPa | T4 | |
Tensile strength | 210.0 MPa Show Material materials with Tensile strength of 210.0 MPa | T4 | |
Yield strength | 100.0 MPa Show Material materials with Yield strength of 100.0 MPa | T4 |
Thermal
Property | Value | Condition | Comment |
---|---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T4 | |
Melting point | 610.0 °C Show Material materials with Melting point of 610.0 °C | T4 | |
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | T4 | |
Thermal conductivity | 170.0 - 220.0 W/(m·K) Show Material materials with Thermal conductivity of 170.0 - 220.0 W/(m·K) | Typical for Wrought 6000 Series Aluminium |
Electrical
Property | Value | Comment |
---|---|---|
Electrical conductivity | 21000000.0 - 34000000.0 S/m Show Material materials with Electrical conductivity of 21000000.0 - 34000000.0 S/m | Typical for Wrought 6000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5e-08 Ω·m Show Material materials with Electrical resistivity of 2.9e-08 - 5e-08 Ω·m | Typical for Wrought 6000 Series Aluminium |
Chemical properties
Property | Value | Condition |
---|---|---|
Aluminium | 97.5 - 99.0 % Show Material materials with Aluminium of 97.5 - 99.0 % | T4 |
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | T4 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | T4 |
Iron | 0.35 % Show Material materials with Iron of 0.35 % | T4 |
Magnesium | 0.4 - 0.6 % Show Material materials with Magnesium of 0.4 - 0.6 % | T4 |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % | T4 |
Other | 0.15 % Show Material materials with Other of 0.15 % | T4 |
Silicon | 0.6 - 0.9 % Show Material materials with Silicon of 0.6 - 0.9 % | T4 |
Titanium | 0.1 % Show Material materials with Titanium of 0.1 % | T4 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | T4 |
Technological properties
Property | ||
---|---|---|
Workability | Excellent workability. |