General
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Compressive modulus | 69.6 MPa Show Material materials with Compressive modulus of 69.6 MPa | T5 | ||
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | T5 | ||
Elongation | 8.0 % Show Material materials with Elongation of 8.0 % | T5 | AA Standards, ASTM B221 | A50 |
9.0 % Show Material materials with Elongation of 9.0 % | T5 | AA Standards, ASTM B221 | A100 | |
9.6 % Show Material materials with Elongation of 9.6 % | T5 | |||
10.0 % Show Material materials with Elongation of 10.0 % | T5 | AA Standards, ASTM B221 | A50 | |
Fatigue strength | 97 MPa Show Material materials with Fatigue strength of 97 MPa | T5 | Min., for 5x10⁸ cycles | |
Hardness, Brinell | 95.0 [-] Show Material materials with Hardness, Brinell of 95.0 [-] | T5 | 500 kg load, 10 mm ball | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Shear strength | 205.0 MPa Show Material materials with Shear strength of 205.0 MPa | T5 | ||
Tensile strength | 260.0 MPa Show Material materials with Tensile strength of 260.0 MPa | T5 | AA Standards, ASTM B221 | |
290.0 MPa Show Material materials with Tensile strength of 290.0 MPa | T5 | |||
Yield strength | 240.0 MPa Show Material materials with Yield strength of 240.0 MPa | T5 | AA Standards, ASTM B221 | RP02 |
270.0 MPa Show Material materials with Yield strength of 270.0 MPa | T5 |
Thermal
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T5 | ||
20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | T5 | AA Standards, ASTM B221 | |
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | T5 | AA Standards, ASTM B221 | |
Melting point | 605.0 - 655.0 °C Show Material materials with Melting point of 605.0 - 655.0 °C | T5 | AA Standards, ASTM B221 | |
610.0 °C Show Material materials with Melting point of 610.0 °C | T5 | |||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | T5 | ||
Thermal conductivity | 180.0 - 188.0 W/(m·K) Show Material materials with Thermal conductivity of 180.0 - 188.0 W/(m·K) | T5 | AA Standards, ASTM B221 | |
180.0 W/(m·K) Show Material materials with Thermal conductivity of 180.0 W/(m·K) | T5 |
Electrical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Electrical conductivity | 27000000.0 - 28000000.0 S/m Show Material materials with Electrical conductivity of 27000000.0 - 28000000.0 S/m | T5 | AA Standards, ASTM B221 | |
28000000 S/m Show Material materials with Electrical conductivity of 28000000 S/m | T5 | Typical/derived value | ||
Electrical resistivity | 3.5e-08 Ω·m Show Material materials with Electrical resistivity of 3.5e-08 Ω·m | T5 | Typical value | |
3.57e-08 - 3.7e-08 Ω·m Show Material materials with Electrical resistivity of 3.57e-08 - 3.7e-08 Ω·m | T5 | AA Standards, ASTM B221 | ||
Specific Electrical conductivity | 49.0 % IACS Show Material materials with Specific Electrical conductivity of 49.0 % IACS | T5 | Typical value |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 97.5 - 99.0 % Show Material materials with Aluminium of 97.5 - 99.0 % | T5 | |
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | T5 | AA Standards, ASTM B221 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | T5 | AA Standards, ASTM B221 |
Iron | 0.35 % Show Material materials with Iron of 0.35 % | T5 | AA Standards, ASTM B221 |
0.35 % Show Material materials with Iron of 0.35 % | T5 | ||
Magnesium | 0.4 - 0.6 % Show Material materials with Magnesium of 0.4 - 0.6 % | T5 | AA Standards, ASTM B221 |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % | T5 | AA Standards, ASTM B221 |
Other | 0.15 % Show Material materials with Other of 0.15 % | T5 | |
Silicon | 0.6 - 0.9 % Show Material materials with Silicon of 0.6 - 0.9 % | T5 | AA Standards, ASTM B221 |
Titanium | 0.1 % Show Material materials with Titanium of 0.1 % | T5 | AA Standards, ASTM B221 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | T5 | AA Standards, ASTM B221 |
Technological properties
Property | ||
---|---|---|
Brazing | general: possible with commercial processes and methods | |
Workability | Excellent workability. |