General
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Bending Fatigue Strength | 60.0 MPa Show Material materials with Bending Fatigue Strength of 60.0 MPa | O | AA Standards | |
Compressive modulus | 69.7 MPa Show Material materials with Compressive modulus of 69.7 MPa | O | ||
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
69 GPa Show Material materials with Elastic modulus of 69 GPa | O | |||
Elongation | 10.0 % Show Material materials with Elongation of 10.0 % | O | AA Standards, ASTM B209 | A50 |
12.0 % Show Material materials with Elongation of 12.0 % | O | AA Standards, ASTM B209 | A50 | |
13.0 % Show Material materials with Elongation of 13.0 % | O | AA Standards, ASTM B210, ASTM B483 | A100 | |
14.0 % Show Material materials with Elongation of 14.0 % | O | AA Standards, ASTM B209 | A50 | |
14.0 % Show Material materials with Elongation of 14.0 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 | A100 | |
15.0 % Show Material materials with Elongation of 15.0 % | O | AA Standards, ASTM B210, ASTM B483 | A50 | |
16.0 % Show Material materials with Elongation of 16.0 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B313, ASTM B345 | A50 | |
16.0 % Show Material materials with Elongation of 16.0 % | O | AA Standards, ASTM B209, ASTM B211 | A100 | |
17.0 % Show Material materials with Elongation of 17.0 % | O | |||
18.0 % Show Material materials with Elongation of 18.0 % | O | AA Standards, ASTM B209, ASTM B211 | A50 | |
20.0 % Show Material materials with Elongation of 20.0 % | O | |||
25.0 % Show Material materials with Elongation of 25.0 % | O | AA Standards | A50 | |
27.0 % Show Material materials with Elongation of 27.0 % | O | AA Standards | A100 | |
27.5 % Show Material materials with Elongation of 27.5 % | O | |||
Hardness, Brinell | 30.0 [-] Show Material materials with Hardness, Brinell of 30.0 [-] | O | AA Standards | |
30.0 [-] Show Material materials with Hardness, Brinell of 30.0 [-] | O | 500 kg load, 10 mm ball | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | O | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Shear strength | 83.0 MPa Show Material materials with Shear strength of 83.0 MPa | O | ||
Tensile strength | 125.0 MPa Show Material materials with Tensile strength of 125.0 MPa | O | AA Standards | |
125 MPa Show Material materials with Tensile strength of 125 MPa | O | |||
130.0 MPa Show Material materials with Tensile strength of 130.0 MPa | O | |||
150.0 MPa Show Material materials with Tensile strength of 150.0 MPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B483 | ||
155.0 MPa Show Material materials with Tensile strength of 155.0 MPa | O | AA Standards, ASTM B211, ASTM B316 | ||
228.0 MPa Show Material materials with Tensile strength of 228.0 MPa | O | |||
Yield strength | 55.0 MPa Show Material materials with Yield strength of 55.0 MPa | O | AA Standards | RP02 |
55 MPa Show Material materials with Yield strength of 55 MPa | O | RP02 | ||
75.0 MPa Show Material materials with Yield strength of 75.0 MPa | O | |||
85.0 MPa Show Material materials with Yield strength of 85.0 MPa | O | AA Standards, ASTM B209 | RP02 | |
95.0 MPa Show Material materials with Yield strength of 95.0 MPa | O | AA Standards, ASTM B210, ASTM B483 | RP02 | |
103.0 MPa Show Material materials with Yield strength of 103.0 MPa | O | |||
110.0 MPa Show Material materials with Yield strength of 110.0 MPa | O | AA Standards, ASTM B221, ASTM B241 | RP02 |
Thermal
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Coefficient of thermal expansion | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | O | ||
2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | O | |||
20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
Melting point | 580.0 - 650.0 °C Show Material materials with Melting point of 580.0 - 650.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
580.0 °C Show Material materials with Melting point of 580.0 °C | O | |||
Specific heat capacity | 896.0 J/(kg·K) Show Material materials with Specific heat capacity of 896.0 J/(kg·K) | O | ||
900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | O | |||
Thermal conductivity | 155.0 - 180.0 W/(m·K) Show Material materials with Thermal conductivity of 155.0 - 180.0 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
170.0 W/(m·K) Show Material materials with Thermal conductivity of 170.0 W/(m·K) | O | |||
180.0 W/(m·K) Show Material materials with Thermal conductivity of 180.0 W/(m·K) | O |
Electrical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Electrical conductivity | 23000000.0 - 27000000.0 S/m Show Material materials with Electrical conductivity of 23000000.0 - 27000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
27000000 S/m Show Material materials with Electrical conductivity of 27000000 S/m | O | Typical value | ||
Electrical resistivity | 3.7e-08 - 4.35e-08 Ω·m Show Material materials with Electrical resistivity of 3.7e-08 - 4.35e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
3.7e-08 Ω·m Show Material materials with Electrical resistivity of 3.7e-08 Ω·m | O | Typical value | ||
Specific Electrical conductivity | 47.0 % IACS Show Material materials with Specific Electrical conductivity of 47.0 % IACS | O | Typical/Derived value |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 95.9 - 98.6 % Show Material materials with Aluminium of 95.9 - 98.6 % | O | |
Chromium | 0.04 - 0.35 % Show Material materials with Chromium of 0.04 - 0.35 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Copper | 0.15 - 0.4 % Show Material materials with Copper of 0.15 - 0.4 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
0.7 % Show Material materials with Iron of 0.7 % | O | ||
Magnesium | 0.8 - 1.2 % Show Material materials with Magnesium of 0.8 - 1.2 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Manganese | 0.15 % Show Material materials with Manganese of 0.15 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Other | 0.15 % Show Material materials with Other of 0.15 % | O | |
Silicon | 0.4 - 0.8 % Show Material materials with Silicon of 0.4 - 0.8 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Technological properties
Property | ||
---|---|---|
Brazing | general: possible with commercial processes and methods | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (O, T6, T651, T652, T6510, T6511), no damage during operation, limited damage during laboratory tests (T4, T451, T4510, T4511), general: good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor (O), sufficient (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511) | |
Workability | general (condition): good (O), acceptable (T4, T451, T4510, T4511), poor(T6, T651, T652, T6510, T6511) |