Properties
General
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Compressive modulus | 69.7 MPa Show Material materials with Compressive modulus of 69.7 MPa | T83 | ||
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | T83 | AA Standards, ASTM B210, ASTM B483 | |
69 GPa Show Material materials with Elastic modulus of 69 GPa | T83 | |||
Elongation | 7.4 % Show Material materials with Elongation of 7.4 % | T83 | ||
9 % Show Material materials with Elongation of 9 % | T83 | |||
Hardness, Brinell | 82.0 [-] Show Material materials with Hardness, Brinell of 82.0 [-] | T83 | 500 kg load, 10 mm ball | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Shear strength | 152.0 MPa Show Material materials with Shear strength of 152.0 MPa | T83 | ||
Tensile strength | 230.0 MPa Show Material materials with Tensile strength of 230.0 MPa | T83 | AA Standards, ASTM B210, ASTM B483 | |
255 MPa Show Material materials with Tensile strength of 255 MPa | T83 | |||
260.0 MPa Show Material materials with Tensile strength of 260.0 MPa | T83 | |||
Yield strength | 205.0 MPa Show Material materials with Yield strength of 205.0 MPa | T83 | AA Standards, ASTM B210, ASTM B483 | RP02 |
240 MPa Show Material materials with Yield strength of 240 MPa | T83 | RP02 | ||
240.0 MPa Show Material materials with Yield strength of 240.0 MPa | T83 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T83 | ||
20 °C | 2.3399999999999996e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3399999999999996e-05 1/K | T83 | AA Standards, ASTM B210, ASTM B483 | |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3399999999999996e-05 1/K | T83 | AA Standards, ASTM B210, ASTM B483 | |
Melting point | 615.0 - 655.0 °C Show Material materials with Melting point of 615.0 - 655.0 °C | T83 | AA Standards, ASTM B210, ASTM B483 | |
620.0 °C Show Material materials with Melting point of 620.0 °C | T83 | |||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | T83 | ||
Thermal conductivity | 193.0 - 218.0 W/(m·K) Show Material materials with Thermal conductivity of 193.0 - 218.0 W/(m·K) | T83 | AA Standards, ASTM B210, ASTM B483 | |
200.0 W/(m·K) Show Material materials with Thermal conductivity of 200.0 W/(m·K) | T83 |
Electrical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Electrical conductivity | 29000000.0 - 34000000.0 S/m Show Material materials with Electrical conductivity of 29000000.0 - 34000000.0 S/m | T83 | AA Standards, ASTM B210, ASTM B483 | |
31000000 S/m Show Material materials with Electrical conductivity of 31000000 S/m | T83 | Typical value | ||
Electrical resistivity | 2.94e-08 - 3.45e-08 Ω·m Show Material materials with Electrical resistivity of 2.94e-08 - 3.45e-08 Ω·m | T83 | AA Standards, ASTM B210, ASTM B483 | |
3.2e-08 Ω·m Show Material materials with Electrical resistivity of 3.2e-08 Ω·m | T83 | Typical value | ||
Specific Electrical conductivity | 53.0 % IACS Show Material materials with Specific Electrical conductivity of 53.0 % IACS | T83 | Typical/Derived value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 97.5 - 99.4 % Show Material materials with Aluminium of 97.5 - 99.4 % | T83 | |
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | T83 | AA Standards, ASTM B210, ASTM B483 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | T83 | AA Standards, ASTM B210, ASTM B483 |
Iron | 0.35 % Show Material materials with Iron of 0.35 % | T83 | AA Standards, ASTM B210, ASTM B483 |
0.35 % Show Material materials with Iron of 0.35 % | T83 | ||
Magnesium | 0.45 - 0.9 % Show Material materials with Magnesium of 0.45 - 0.9 % | T83 | AA Standards, ASTM B210, ASTM B483 |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % | T83 | AA Standards, ASTM B210, ASTM B483 |
Other | 0.15 % Show Material materials with Other of 0.15 % | T83 | |
Silicon | 0.2 - 0.6 % Show Material materials with Silicon of 0.2 - 0.6 % | T83 | AA Standards, ASTM B210, ASTM B483 |
Titanium | 0.1 % Show Material materials with Titanium of 0.1 % | T83 | AA Standards, ASTM B210, ASTM B483 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | T83 | AA Standards, ASTM B210, ASTM B483 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (T1, T4), sufficient (T5, T452, T6, T83, T831, T832) | |
| Workability | general (condition): acceptable (T1, T4, T5, T452), poor(T6, T83, T831, T832) | |