Properties
General
| Property | Value | Temperature |
|---|---|---|
Density | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ at 23.0 °C | 23.0 °C |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Elastic modulus | 72 GPa Show Material materials with Elastic modulus of 72 GPa at 23.0 °C | 23.0 °C | |
Elongation | 9.2 % Show Material materials with Elongation of 9.2 % at 23.0 °C | 23.0 °C | |
Plane-Strain Fracture Toughnes | 22 - 35 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C | 23.0 °C | Typical for Wrought 6000 Series Aluminium |
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] at 23.0 °C | 23.0 °C | Typical for Wrought 6000 Series Aluminium |
Shear modulus | 26 - 26.5 GPa Show Material materials with Shear modulus of 26 - 26.5 GPa at 23.0 °C | 23.0 °C | Typical for Wrought 6000 Series Aluminium |
Tensile strength | 310 MPa Show Material materials with Tensile strength of 310 MPa at 23.0 °C | 23.0 °C | |
Yield strength | 260 MPa Show Material materials with Yield strength of 260 MPa at 23.0 °C | 23.0 °C |
Thermal
| Property | Value | Temperature | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 2.3E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.3E-5 1/K at 23.0 °C | 23.0 °C | |
Melting point | 580 °C Show Material materials with Melting point of 580 °C | ||
Specific heat capacity | 890 J/(kg·K) Show Material materials with Specific heat capacity of 890 J/(kg·K) at 23.0 °C | 23.0 °C | |
Thermal conductivity | 170 - 220 W/(m·K) Show Material materials with Thermal conductivity of 170 - 220 W/(m·K) at 23.0 °C | 23.0 °C | Typical for Wrought 6000 Series Aluminium |
Electrical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Electrical conductivity | 2.10E+7 - 3.40E+7 S/m Show Material materials with Electrical conductivity of 2.10E+7 - 3.40E+7 S/m at 23.0 °C | 23.0 °C | Typical for Wrought 6000 Series Aluminium |
Electrical resistivity | 2.9E-8 - 5E-8 Ω·m Show Material materials with Electrical resistivity of 2.9E-8 - 5E-8 Ω·m at 23.0 °C | 23.0 °C | Typical for Wrought 6000 Series Aluminium |
Chemical properties
| Property | ||
|---|---|---|
Aluminium | 95.2 - 98.3 % | |
Chromium | 0 - 0.25 % | |
Copper | 0 - 0.1 % | |
Iron | 0 - 0.5 % | |
Magnesium | 0.6 - 1.2 % | |
Manganese | 0.4 - 1 % | |
Other | 0 - 0.15 % | |
Silicon | 0.7 - 1.3 % | |
Titanium | 0 - 0.1 % | |
Zinc | 0 - 0.2 % |
Technological properties
| Property | ||
|---|---|---|
| Workability | Excellent workability. | |