AA Standards Grade 7075 T6

View suppliers (130)
Want to keep this datasheet? Save it now in your required format

Description

AA 7075 is a high-strength alloy that offers good stress-corrosion cracking resistance. Known as a mainstay in the aerospace industry since it was introduced, Aluminum 7075 brings moderate toughness as well as an excellent strength-to-weight ratio. It is also important to note that at sub-zero temperatures Aluminum 7075 increases in strength.

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials,Matmatch,WroughtAl_ElectricalResistivity,Righton Blackburns.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionShapeRelated Standards

Density

2.8 g/cm³

Show Material materials with Density of 2.8 g/cm³

T6

Bar, Rod

2.81 g/cm³

Show Material materials with Density of 2.81 g/cm³

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

2.81 g/cm³

Show Material materials with Density of 2.81 g/cm³

T6

3.1 g/cm³

Show Material materials with Density of 3.1 g/cm³

T6

Mechanical

PropertyTemperatureValueConditionRelated StandardsShapeComment

Bending Fatigue Strength

160.0 MPa

Show Material materials with Bending Fatigue Strength of 160.0 MPa

T6

AA Standards

Compressive modulus

72.4 MPa

Show Material materials with Compressive modulus of 72.4 MPa

T6

Elastic modulus

71.0 GPa

Show Material materials with Elastic modulus of 71.0 GPa

T6

72.0 GPa

Show Material materials with Elastic modulus of 72.0 GPa

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

Bar, Rod

72 GPa

Show Material materials with Elastic modulus of 72 GPa

T6

Elongation

-195 °C

9 %

Show Material materials with Elongation of 9 %

T6

Elongation in 50 mm

-80 °C

11 %

Show Material materials with Elongation of 11 %

T6

Elongation in 50 mm

1.0 %

Show Material materials with Elongation of 1.0 %

T6

AA Standards, ASTM B247

A100

2.0 %

Show Material materials with Elongation of 2.0 %

T6

AA Standards, ASTM B247

A50

2.0 %

Show Material materials with Elongation of 2.0 %

T6

AA Standards, ASTM B247

A100

3.0 %

Show Material materials with Elongation of 3.0 %

T6

AA Standards, ASTM B247

A50

3.0 %

Show Material materials with Elongation of 3.0 %

T6

AA Standards, ASTM B247

A100

5.0 %

Show Material materials with Elongation of 5.0 %

T6

AA Standards, ASTM B209

A50

5.0 %

Show Material materials with Elongation of 5.0 %

T6

AA Standards, ASTM B221, ASTM B247

A100

6.0 %

Show Material materials with Elongation of 6.0 %

T6

AA Standards, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

A100

6.8 %

Show Material materials with Elongation of 6.8 %

T6

7.0 %

Show Material materials with Elongation of 7.0 %

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247

Bar, Rod

A50

7.0 %

Show Material materials with Elongation of 7.0 %

T6

AA Standards, ASTM B210, ASTM B247

A100

8.0 %

Show Material materials with Elongation of 8.0 %

T6

AA Standards, ASTM B209, ASTM B210

A50

8.0 %

Show Material materials with Elongation of 8.0 %

T6

AA Standards, ASTM B247

A100

9.0 %

Show Material materials with Elongation of 9.0 %

T6

AA Standards

A100

11.0 %

Show Material materials with Elongation of 11.0 %

T6

AA Standards

A50

11.0 %

Show Material materials with Elongation of 11.0 %

T6

0 °C

11 %

Show Material materials with Elongation of 11 %

T6

Elongation in 50 mm

24 °C

11 %

Show Material materials with Elongation of 11 %

T6

Elongation in 50 mm

100 °C

14 %

Show Material materials with Elongation of 14 %

T6

Elongation in 50 mm

150 °C

30 %

Show Material materials with Elongation of 30 %

T6

Elongation in 50 mm

205 °C

55 %

Show Material materials with Elongation of 55 %

T6

Elongation in 50 mm

260 °C

65 %

Show Material materials with Elongation of 65 %

T6

Elongation in 50 mm

315 °C

70 %

Show Material materials with Elongation of 70 %

T6

Elongation in 50 mm

370 °C

70 %

Show Material materials with Elongation of 70 %

T6

Elongation in 50 mm

Fatigue strength

159 MPa

Show Material materials with Fatigue strength of 159 MPa

T6

for 5x10⁸ cycles

Hardness, Brinell

150.0 [-]

Show Material materials with Hardness, Brinell of 150.0 [-]

T6

AA Standards

150.0 [-]

Show Material materials with Hardness, Brinell of 150.0 [-]

T6

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 7000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

T6

Shear modulus

26.9 GPa

Show Material materials with Shear modulus of 26.9 GPa

T6

Shear strength

331.0 MPa

Show Material materials with Shear strength of 331.0 MPa

T6

Tensile strength

-195 °C

703 MPa

Show Material materials with Tensile strength of 703 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

620 MPa

Show Material materials with Tensile strength of 620 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

450.0 MPa

Show Material materials with Tensile strength of 450.0 MPa

T6

AA Standards, ASTM B247

455.0 MPa

Show Material materials with Tensile strength of 455.0 MPa

T6

AA Standards, ASTM B247

470.0 MPa

Show Material materials with Tensile strength of 470.0 MPa

T6

AA Standards, ASTM B247

475.0 MPa

Show Material materials with Tensile strength of 475.0 MPa

T6

AA Standards, ASTM B247

485.0 MPa

Show Material materials with Tensile strength of 485.0 MPa

T6

AA Standards, ASTM B247

490.0 MPa

Show Material materials with Tensile strength of 490.0 MPa

T6

AA Standards, ASTM B247

495.0 MPa

Show Material materials with Tensile strength of 495.0 MPa

T6

AA Standards, ASTM B247

505.0 MPa

Show Material materials with Tensile strength of 505.0 MPa

T6

AA Standards, ASTM B247

510.0 MPa

Show Material materials with Tensile strength of 510.0 MPa

T6

AA Standards, ASTM B209, ASTM B247

515.0 MPa

Show Material materials with Tensile strength of 515.0 MPa

T6

AA Standards, ASTM B247

525.0 MPa

Show Material materials with Tensile strength of 525.0 MPa

T6

AA Standards, ASTM B209

530.0 MPa

Show Material materials with Tensile strength of 530.0 MPa

T6

AA Standards, ASTM B210, ASTM B211, ASTM B316

540.0 MPa

Show Material materials with Tensile strength of 540.0 MPa

T6

AA Standards, ASTM B209, ASTM B221, ASTM B241

Bar, Rod

560.0 MPa

Show Material materials with Tensile strength of 560.0 MPa

T6

AA Standards, ASTM B221, ASTM B241

570.0 MPa

Show Material materials with Tensile strength of 570.0 MPa

T6

AA Standards

572.0 MPa

Show Material materials with Tensile strength of 572.0 MPa

T6

0 °C

593 MPa

Show Material materials with Tensile strength of 593 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

24 °C

572 MPa

Show Material materials with Tensile strength of 572 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

483 MPa

Show Material materials with Tensile strength of 483 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

215 MPa

Show Material materials with Tensile strength of 215 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

110 MPa

Show Material materials with Tensile strength of 110 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

75 MPa

Show Material materials with Tensile strength of 75 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

55 MPa

Show Material materials with Tensile strength of 55 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

370 °C

40 MPa

Show Material materials with Tensile strength of 40 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Yield strength

-196 °C

634 MPa

Show Material materials with Yield strength of 634 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-80 °C

545 MPa

Show Material materials with Yield strength of 545 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-28 °C

517 MPa

Show Material materials with Yield strength of 517 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

380.0 MPa

Show Material materials with Yield strength of 380.0 MPa

T6

AA Standards, ASTM B247

RP02

385.0 MPa

Show Material materials with Yield strength of 385.0 MPa

T6

AA Standards, ASTM B247

RP02

395.0 MPa

Show Material materials with Yield strength of 395.0 MPa

T6

AA Standards, ASTM B247

RP02

400.0 MPa

Show Material materials with Yield strength of 400.0 MPa

T6

AA Standards, ASTM B247

RP02

405.0 MPa

Show Material materials with Yield strength of 405.0 MPa

T6

AA Standards, ASTM B247

RP02

415.0 MPa

Show Material materials with Yield strength of 415.0 MPa

T6

AA Standards, ASTM B247

RP02

420.0 MPa

Show Material materials with Yield strength of 420.0 MPa

T6

AA Standards, ASTM B247

RP02

425.0 MPa

Show Material materials with Yield strength of 425.0 MPa

T6

AA Standards, ASTM B247

RP02

435.0 MPa

Show Material materials with Yield strength of 435.0 MPa

T6

AA Standards, ASTM B209, ASTM B247

RP02

440.0 MPa

Show Material materials with Yield strength of 440.0 MPa

T6

AA Standards, ASTM B247

RP02

455.0 MPa

Show Material materials with Yield strength of 455.0 MPa

T6

AA Standards, ASTM B210, ASTM B211, ASTM B316

RP02

460.0 MPa

Show Material materials with Yield strength of 460.0 MPa

T6

AA Standards, ASTM B209

RP02

470.0 MPa

Show Material materials with Yield strength of 470.0 MPa

T6

AA Standards, ASTM B209, ASTM B221

RP02

470.0 MPa

Show Material materials with Yield strength of 470.0 MPa

T6

475.0 MPa

Show Material materials with Yield strength of 475.0 MPa

T6

AA Standards, ASTM B209

RP02

480.0 MPa

Show Material materials with Yield strength of 480.0 MPa

T6

Bar, Rod

RP02

485.0 MPa

Show Material materials with Yield strength of 485.0 MPa

T6

AA Standards, ASTM B221, ASTM B241

RP02

490.0 MPa

Show Material materials with Yield strength of 490.0 MPa

T6

AA Standards, ASTM B221

RP02

495.0 MPa

Show Material materials with Yield strength of 495.0 MPa

T6

AA Standards, ASTM B221, ASTM B241

RP02

505.0 MPa

Show Material materials with Yield strength of 505.0 MPa

T6

AA Standards, ASTM B221, ASTM B241

RP02

505.0 MPa

Show Material materials with Yield strength of 505.0 MPa

T6

24 °C

503 MPa

Show Material materials with Yield strength of 503 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

100 °C

448 MPa

Show Material materials with Yield strength of 448 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

149 °C

186 MPa

Show Material materials with Yield strength of 186 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

204 °C

87 MPa

Show Material materials with Yield strength of 87 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

260 °C

62 MPa

Show Material materials with Yield strength of 62 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

316 °C

45 MPa

Show Material materials with Yield strength of 45 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

371 °C

32 MPa

Show Material materials with Yield strength of 32 MPa

T6

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

Thermal

PropertyTemperatureValueConditionRelated StandardsShape

Coefficient of thermal expansion

2.3e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K

T6

2.34e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.34e-05 1/K

T6

20 °C

2.36e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

100 °C

2.36e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

Melting point

475.0 - 635.0 °C

Show Material materials with Melting point of 475.0 - 635.0 °C

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

480.0 °C

Show Material materials with Melting point of 480.0 °C

T6

635.0 °C

Show Material materials with Melting point of 635.0 °C

T6

Bar, Rod

Specific heat capacity

910.0 J/(kg·K)

Show Material materials with Specific heat capacity of 910.0 J/(kg·K)

T6

960.0 J/(kg·K)

Show Material materials with Specific heat capacity of 960.0 J/(kg·K)

T6

Thermal conductivity

130 W/(m·K)

Show Material materials with Thermal conductivity of 130 W/(m·K)

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

130.0 W/(m·K)

Show Material materials with Thermal conductivity of 130.0 W/(m·K)

T6

Bar, Rod

Electrical

PropertyValueConditionRelated StandardsShapeComment

Electrical conductivity

19000000.0 S/m

Show Material materials with Electrical conductivity of 19000000.0 S/m

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

19000000 S/m

Show Material materials with Electrical conductivity of 19000000 S/m

T6

Typical value

Electrical resistivity

4.31e-08 Ω·m

Show Material materials with Electrical resistivity of 4.31e-08 Ω·m

T6

Bar, Rod

5.1500000000000005e-08 Ω·m

Show Material materials with Electrical resistivity of 5.1500000000000005e-08 Ω·m

T6

Typical value

5.22e-08 Ω·m

Show Material materials with Electrical resistivity of 5.22e-08 Ω·m

T6

5.26e-08 Ω·m

Show Material materials with Electrical resistivity of 5.26e-08 Ω·m

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

Specific Electrical conductivity

33.0 % IACS

Show Material materials with Specific Electrical conductivity of 33.0 % IACS

T6

Typical/Derived value

Chemical properties

PropertyValueConditionRelated StandardsShapeComment

Aluminium

86.9 - 91.4 %

Show Material materials with Aluminium of 86.9 - 91.4 %

T6

Chromium

0.18 - 0.28 %

Show Material materials with Chromium of 0.18 - 0.28 %

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

Bar, Rod

Copper

1.2 - 2.0 %

Show Material materials with Copper of 1.2 - 2.0 %

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

Bar, Rod

Iron

0.50 %

Show Material materials with Iron of 0.50 %

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

0.5 %

Show Material materials with Iron of 0.5 %

T6

Bar, Rod

Magnesium

2.1 - 2.9 %

Show Material materials with Magnesium of 2.1 - 2.9 %

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

Bar, Rod

Manganese

0.3 %

Show Material materials with Manganese of 0.3 %

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

Bar, Rod

Other

0.15 %

Show Material materials with Other of 0.15 %

T6

Bar, Rod

Total

Silicon

0.4 %

Show Material materials with Silicon of 0.4 %

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

Bar, Rod

Titanium

0.2 %

Show Material materials with Titanium of 0.2 %

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

Bar, Rod

Zinc

5.1 - 6.1 %

Show Material materials with Zinc of 5.1 - 6.1 %

T6

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

Bar, Rod

Zirconium

0.25 %

Show Material materials with Zirconium of 0.25 %

T6

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O), good to acceptable

Workability

general (condition): not suitable