General
Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | H16 | |
2.705 g/cm³ Show Material materials with Density of 2.705 g/cm³ | H16 | AA Standards, ASTM B209, ASTM B211 |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Bending Fatigue Strength | 45.0 MPa Show Material materials with Bending Fatigue Strength of 45.0 MPa | H16 | AA Standards | |
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H16 | AA Standards, ASTM B209, ASTM B211 | |
69 GPa Show Material materials with Elastic modulus of 69 GPa | H16 | |||
Elongation | 1.0 % Show Material materials with Elongation of 1.0 % | H16 | AA Standards, ASTM B209 | A50 |
2.0 % Show Material materials with Elongation of 2.0 % | H16 | AA Standards, ASTM B209 | A50 | |
4.0 % Show Material materials with Elongation of 4.0 % | H16 | AA Standards, ASTM B209 | A50 | |
5.0 % Show Material materials with Elongation of 5.0 % | H16 | AA Standards, ASTM B209 | A50 | |
5.3 % Show Material materials with Elongation of 5.3 % | H16 | |||
8.0 % Show Material materials with Elongation of 8.0 % | H16 | AA Standards | A50 | |
8 % Show Material materials with Elongation of 8 % | H16 | |||
Fatigue strength | 45 MPa Show Material materials with Fatigue strength of 45 MPa | H16 | for 5x10⁸ cycles | |
Hardness, Brinell | 30.0 [-] Show Material materials with Hardness, Brinell of 30.0 [-] | H16 | AA Standards | |
38.0 [-] Show Material materials with Hardness, Brinell of 38.0 [-] | H16 | 500 kg load, 10 mm ball | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Shear modulus | 25.0 GPa Show Material materials with Shear modulus of 25.0 GPa | H16 | ||
Shear strength | 70.0 MPa Show Material materials with Shear strength of 70.0 MPa | H16 | ||
Tensile strength | 95.0 - 130.0 MPa Show Material materials with Tensile strength of 95.0 - 130.0 MPa | H16 | AA Standards, ASTM B209 | |
110.0 MPa Show Material materials with Tensile strength of 110.0 MPa | H16 | AA Standards, ASTM B211 | ||
110 MPa Show Material materials with Tensile strength of 110 MPa | H16 | |||
115.0 MPa Show Material materials with Tensile strength of 115.0 MPa | H16 | AA Standards | ||
Yield strength | 75.0 MPa Show Material materials with Yield strength of 75.0 MPa | H16 | AA Standards, ASTM B209 | RP02 |
90.0 MPa Show Material materials with Yield strength of 90.0 MPa | H16 | AA Standards, ASTM B211 | RP02 | |
98.0 MPa Show Material materials with Yield strength of 98.0 MPa | H16 | |||
105.0 MPa Show Material materials with Yield strength of 105.0 MPa | H16 | AA Standards | RP02 | |
105 MPa Show Material materials with Yield strength of 105 MPa | H16 | RP02 |
Thermal
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H16 | ||
20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | H16 | AA Standards, ASTM B209, ASTM B211 | |
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | H16 | AA Standards, ASTM B209, ASTM B211 | |
Melting point | 645.0 - 655.0 °C Show Material materials with Melting point of 645.0 - 655.0 °C | H16 | AA Standards, ASTM B209, ASTM B211 | |
650.0 °C Show Material materials with Melting point of 650.0 °C | H16 | |||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | H16 | ||
Thermal conductivity | 230.0 - 234.0 W/(m·K) Show Material materials with Thermal conductivity of 230.0 - 234.0 W/(m·K) | H16 | AA Standards, ASTM B209, ASTM B211 | |
230.0 W/(m·K) Show Material materials with Thermal conductivity of 230.0 W/(m·K) | H16 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 35000000.0 - 36000000.0 S/m Show Material materials with Electrical conductivity of 35000000.0 - 36000000.0 S/m | H16 | AA Standards, ASTM B209, ASTM B211 |
Electrical resistivity | 2.78e-08 - 2.86e-08 Ω·m Show Material materials with Electrical resistivity of 2.78e-08 - 2.86e-08 Ω·m | H16 | AA Standards, ASTM B209, ASTM B211 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 99.6 % Show Material materials with Aluminium of 99.6 % | H16 | AA Standards, ASTM B209, ASTM B211 |
99.6 - 100.0 % Show Material materials with Aluminium of 99.6 - 100.0 % | H16 | ||
Copper | 0.05 % Show Material materials with Copper of 0.05 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Iron | 0.35 % Show Material materials with Iron of 0.35 % | H16 | AA Standards, ASTM B209, ASTM B211 |
0.35 % Show Material materials with Iron of 0.35 % | H16 | ||
Magnesium | 0.03 % Show Material materials with Magnesium of 0.03 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Manganese | 0.03 % Show Material materials with Manganese of 0.03 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Silicon | 0.25 % Show Material materials with Silicon of 0.25 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Titanium | 0.03 % Show Material materials with Titanium of 0.03 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Vanadium | 0.05 % Show Material materials with Vanadium of 0.05 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Zinc | 0.05 % Show Material materials with Zinc of 0.05 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Technological properties
Property | ||
---|---|---|
Brazing | general: possible with commercial processes and methods | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
Workability | general (condition): good (O, H12, H14), acceptable (H16, H18) |