AA Standards Grade 7075 T7351

View suppliers (130)
Alternative and trade names
FORMODAL® BM-7075, 7075 T751
Want to keep this datasheet? Save it now in your required format

Description

AA 7075 is a high-strength alloy that offers good stress-corrosion cracking resistance. Known as a mainstay in the aerospace industry since it was introduced, Aluminum 7075 brings moderate toughness as well as an excellent strength-to-weight ratio. It is also important to note that at sub-zero temperatures Aluminum 7075 increases in strength.

Related Standards

Equivalent Materials

This material data has been provided by ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials,WroughtAl_ElectricalResistivity,AluKey,MakeItFrom.com,BIKA,Righton Blackburns.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionShape

Density

2.8 g/cm³

Show Material materials with Density of 2.8 g/cm³

T7351

Sheet, Plate

2.81 g/cm³

Show Material materials with Density of 2.81 g/cm³

T7351

2.81 g/cm³

Show Material materials with Density of 2.81 g/cm³

T7351

Bar

3.1 g/cm³

Show Material materials with Density of 3.1 g/cm³

T7351

Surface roughness

0.4

Show Material materials with Surface roughness of 0.4

T7351

Sheet, Plate

Dimension

PropertyValueConditionThicknessShape

Thickness

8 mm

Show Material materials with Thickness of 8 mm

T7351

8 mm

Sheet, Plate

100 mm

Show Material materials with Thickness of 100 mm

T7351

100 mm

Sheet, Plate

Mechanical

PropertyTemperatureValueConditionShapeRelated StandardsComment

Elastic modulus

72.0 GPa

Show Material materials with Elastic modulus of 72.0 GPa

T7351

Sheet, Plate, Bar

Elongation

-195 °C

14 %

Show Material materials with Elongation of 14 %

T7351

Elongation in 50 mm

-80 °C

14 %

Show Material materials with Elongation of 14 %

T7351

Elongation in 50 mm

5.0 - 6.0 %

Show Material materials with Elongation of 5.0 - 6.0 %

T7351

Sheet, Plate

5.0 %

Show Material materials with Elongation of 5.0 %

T7351

AA Standards, ASTM B209

A100

6.0 %

Show Material materials with Elongation of 6.0 %

T7351

AA Standards, ASTM B209

A100

7.0 %

Show Material materials with Elongation of 7.0 %

T7351

AA Standards, ASTM B211

A100

7.0 %

Show Material materials with Elongation of 7.0 %

T7351

Sheet, Plate

AA Standards, ASTM B209

A50

7.2 %

Show Material materials with Elongation of 7.2 %

T7351

8.0 %

Show Material materials with Elongation of 8.0 %

T7351

AA Standards, ASTM B211

A50

9.0 %

Show Material materials with Elongation of 9.0 %

T7351

AA Standards, ASTM B211

A100

10.0 %

Show Material materials with Elongation of 10.0 %

T7351

Bar

AA Standards, ASTM B211

A50

0 °C

13 %

Show Material materials with Elongation of 13 %

T7351

Elongation in 50 mm

24 °C

13 %

Show Material materials with Elongation of 13 %

T7351

Elongation in 50 mm

100 °C

15 %

Show Material materials with Elongation of 15 %

T7351

Elongation in 50 mm

150 °C

30 %

Show Material materials with Elongation of 30 %

T7351

Elongation in 50 mm

205 °C

55 %

Show Material materials with Elongation of 55 %

T7351

Elongation in 50 mm

260 °C

65 %

Show Material materials with Elongation of 65 %

T7351

Elongation in 50 mm

315 °C

70 %

Show Material materials with Elongation of 70 %

T7351

Elongation in 50 mm

370 °C

70 %

Show Material materials with Elongation of 70 %

T7351

Elongation in 50 mm

Hardness, HBW

126.0 - 140.0 [-]

Show Material materials with Hardness, HBW of 126.0 - 140.0 [-]

T7351

Sheet, Plate

Plane-Strain Fracture Toughnes

-196 °C

32.1 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 32.1 MPa·√m

T7351

For plate in T-L direction

24 °C

35.9 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 35.9 MPa·√m

T7351

For plate in T-L direction

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 7000 Series Aluminium

Shear modulus

26.4 - 27.1 GPa

Show Material materials with Shear modulus of 26.4 - 27.1 GPa

Typical for Wrought 7000 Series Aluminium

Tensile strength

-195 °C

635 MPa

Show Material materials with Tensile strength of 635 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

545 MPa

Show Material materials with Tensile strength of 545 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

420.0 MPa

Show Material materials with Tensile strength of 420.0 MPa

T7351

AA Standards, ASTM B209

430.0 - 475.0 MPa

Show Material materials with Tensile strength of 430.0 - 475.0 MPa

T7351

Sheet, Plate

435.0 MPa

Show Material materials with Tensile strength of 435.0 MPa

T7351

AA Standards, ASTM B209

440.0 MPa

Show Material materials with Tensile strength of 440.0 MPa

T7351

AA Standards, ASTM B209, ASTM B211

455.0 MPa

Show Material materials with Tensile strength of 455.0 MPa

T7351

AA Standards, ASTM B209, ASTM B211

469.0 MPa

Show Material materials with Tensile strength of 469.0 MPa

T7351

Bar

470.0 MPa

Show Material materials with Tensile strength of 470.0 MPa

T7351

AA Standards, ASTM B211

475.0 MPa

Show Material materials with Tensile strength of 475.0 MPa

T7351

AA Standards, ASTM B209

520.0 MPa

Show Material materials with Tensile strength of 520.0 MPa

T7351

0 °C

525 MPa

Show Material materials with Tensile strength of 525 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

24 °C

503 MPa

Show Material materials with Tensile strength of 503 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

435 MPa

Show Material materials with Tensile strength of 435 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

215 MPa

Show Material materials with Tensile strength of 215 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

110 MPa

Show Material materials with Tensile strength of 110 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

75 MPa

Show Material materials with Tensile strength of 75 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

55 MPa

Show Material materials with Tensile strength of 55 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

370 °C

40 MPa

Show Material materials with Tensile strength of 40 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Yield strength

-196 °C

496 MPa

Show Material materials with Yield strength of 496 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-80 °C

462 MPa

Show Material materials with Yield strength of 462 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-28 °C

448 MPa

Show Material materials with Yield strength of 448 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

330.0 MPa

Show Material materials with Yield strength of 330.0 MPa

T7351

AA Standards, ASTM B209

RP02

340.0 MPa

Show Material materials with Yield strength of 340.0 MPa

T7351

AA Standards, ASTM B209

RP02

340.0 - 390.0 MPa

Show Material materials with Yield strength of 340.0 - 390.0 MPa

T7351

Sheet, Plate

360.0 MPa

Show Material materials with Yield strength of 360.0 MPa

T7351

AA Standards, ASTM B209

RP02

380.0 MPa

Show Material materials with Yield strength of 380.0 MPa

T7351

AA Standards, ASTM B211

RP02

386.0 MPa

Show Material materials with Yield strength of 386.0 MPa

T7351

Bar

RP02

390.0 MPa

Show Material materials with Yield strength of 390.0 MPa

T7351

AA Standards, ASTM B209

RP02

420.0 MPa

Show Material materials with Yield strength of 420.0 MPa

T7351

425.0 MPa

Show Material materials with Yield strength of 425.0 MPa

T7351

AA Standards, ASTM B211

RP02

24 °C

434 MPa

Show Material materials with Yield strength of 434 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

100 °C

400 MPa

Show Material materials with Yield strength of 400 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

149 °C

186 MPa

Show Material materials with Yield strength of 186 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

204 °C

90 MPa

Show Material materials with Yield strength of 90 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

260 °C

62 MPa

Show Material materials with Yield strength of 62 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

316 °C

45 MPa

Show Material materials with Yield strength of 45 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

371 °C

32 MPa

Show Material materials with Yield strength of 32 MPa

T7351

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

Thermal

PropertyTemperatureValueConditionShapeComment

Coefficient of thermal expansion

2.3e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K

T7351

2.35e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.35e-05 1/K

T7351

Bar

100 °C

0.0000234 1/K

Show Material materials with Coefficient of thermal expansion of 0.0000234 1/K

T7351

Sheet, Plate

Mean values between 20°C and the mentioned temperature

200 °C

0.0000243 1/K

Show Material materials with Coefficient of thermal expansion of 0.0000243 1/K

T7351

Sheet, Plate

Mean values between 20°C and the mentioned temperature

300 °C

0.0000252 1/K

Show Material materials with Coefficient of thermal expansion of 0.0000252 1/K

T7351

Sheet, Plate

Mean values between 20°C and the mentioned temperature

Melting point

480.0 °C

Show Material materials with Melting point of 480.0 °C

T7351

635.0 °C

Show Material materials with Melting point of 635.0 °C

T7351

Bar

Specific heat capacity

862.0 J/(kg·K)

Show Material materials with Specific heat capacity of 862.0 J/(kg·K)

T7351

Sheet, Plate

910.0 J/(kg·K)

Show Material materials with Specific heat capacity of 910.0 J/(kg·K)

T7351

Thermal conductivity

130.0 W/(m·K)

Show Material materials with Thermal conductivity of 130.0 W/(m·K)

T7351

130.0 - 160.0 W/(m·K)

Show Material materials with Thermal conductivity of 130.0 - 160.0 W/(m·K)

T7351

Sheet, Plate

134.0 - 160.0 W/(m·K)

Show Material materials with Thermal conductivity of 134.0 - 160.0 W/(m·K)

T7351

Bar

Electrical

PropertyValueConditionShapeComment

Electrical conductivity

19000000.0 - 23000000.0 S/m

Show Material materials with Electrical conductivity of 19000000.0 - 23000000.0 S/m

T7351

Sheet, Plate

23000000 S/m

Show Material materials with Electrical conductivity of 23000000 S/m

T7351

Typical/derived value

Electrical resistivity

4.3099999999999996e-08 Ω·m

Show Material materials with Electrical resistivity of 4.3099999999999996e-08 Ω·m

T7351

Typical value

4.31e-08 Ω·m

Show Material materials with Electrical resistivity of 4.31e-08 Ω·m

T7351

Bar

Specific Electrical conductivity

40.0 % IACS

Show Material materials with Specific Electrical conductivity of 40.0 % IACS

T7351

Typical value

Chemical properties

PropertyValueConditionRelated StandardsShapeComment

Aluminium

86.9 - 91.4 %

Show Material materials with Aluminium of 86.9 - 91.4 %

T7351

Chromium

0.18 - 0.28 %

Show Material materials with Chromium of 0.18 - 0.28 %

T7351

AA Standards, ASTM B209, ASTM B211

Sheet, Plate, Bar

Copper

1.2 - 2.0 %

Show Material materials with Copper of 1.2 - 2.0 %

T7351

AA Standards, ASTM B209, ASTM B211

Sheet, Plate, Bar

Iron

0.50 %

Show Material materials with Iron of 0.50 %

T7351

AA Standards, ASTM B209, ASTM B211

0.5 %

Show Material materials with Iron of 0.5 %

T7351

Sheet, Plate, Bar

Magnesium

2.1 - 2.9 %

Show Material materials with Magnesium of 2.1 - 2.9 %

T7351

AA Standards, ASTM B209, ASTM B211

Sheet, Plate, Bar

Manganese

0.3 %

Show Material materials with Manganese of 0.3 %

T7351

AA Standards, ASTM B209, ASTM B211

Sheet, Plate, Bar

Other

0.15 %

Show Material materials with Other of 0.15 %

T7351

Sheet, Plate, Bar

Total

Silicon

0.4 %

Show Material materials with Silicon of 0.4 %

T7351

AA Standards, ASTM B209, ASTM B211

Sheet, Plate, Bar

Titanium

0.2 %

Show Material materials with Titanium of 0.2 %

T7351

AA Standards, ASTM B209, ASTM B211

Sheet, Plate, Bar

Zinc

5.1 - 6.1 %

Show Material materials with Zinc of 5.1 - 6.1 %

T7351

AA Standards, ASTM B209, ASTM B211

Sheet, Plate, Bar

Zirconium

0.25 %

Show Material materials with Zirconium of 0.25 %

T7351

Technological properties

Property
Anodizing

moderate

Application areas

Tool making, mould making and model making; Aerospace; Military technology

Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O), good to acceptable

Soldering general

not recommended

Welding

Resistance welding: good

Workability

general (condition): not suitable