Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.71 g/cm³ Show Material materials with Density of 2.71 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
2.71 g/cm³ Show Material materials with Density of 2.71 g/cm³ | O | ||
2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | O |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 35.0 MPa Show Material materials with Bending Fatigue Strength of 35.0 MPa | O | AA Standards | ||
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
69 GPa Show Material materials with Elastic modulus of 69 GPa | O | ||||
Elongation | -195 °C | 50 % Show Material materials with Elongation of 50 % | O | Elongation in 50 mm | |
-80 °C | 43 % Show Material materials with Elongation of 43 % | O | Elongation in 50 mm | ||
15.0 % Show Material materials with Elongation of 15.0 % | O | AA Standards, ASTM B209 | A50 | ||
17.0 % Show Material materials with Elongation of 17.0 % | O | AA Standards, ASTM B209 | A50 | ||
22.0 % Show Material materials with Elongation of 22.0 % | O | AA Standards, ASTM B209, ASTM B313 | A50 | ||
22.0 % Show Material materials with Elongation of 22.0 % | O | AA Standards, ASTM B211, ASTM B241 | A100 | ||
25.0 % Show Material materials with Elongation of 25.0 % | O | AA Standards, ASTM B211, ASTM B241 | A50 | ||
25.0 % Show Material materials with Elongation of 25.0 % | O | AA Standards, ASTM B209 | A100 | ||
28.0 % Show Material materials with Elongation of 28.0 % | O | AA Standards, ASTM B209, ASTM B547 | A50 | ||
30.0 % Show Material materials with Elongation of 30.0 % | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | ||
31.0 % Show Material materials with Elongation of 31.0 % | O | ||||
35.0 % Show Material materials with Elongation of 35.0 % | O | AA Standards | A50 | ||
40.0 % Show Material materials with Elongation of 40.0 % | O | ||||
0 °C | 40 % Show Material materials with Elongation of 40 % | O | Elongation in 50 mm | ||
42.0 % Show Material materials with Elongation of 42.0 % | O | AA Standards | A100 | ||
24 °C | 40 % Show Material materials with Elongation of 40 % | O | Elongation in 50 mm | ||
100 °C | 45 % Show Material materials with Elongation of 45 % | O | Elongation in 50 mm | ||
150 °C | 55 % Show Material materials with Elongation of 55 % | O | Elongation in 50 mm | ||
205 °C | 65 % Show Material materials with Elongation of 65 % | O | Elongation in 50 mm | ||
260 °C | 75 % Show Material materials with Elongation of 75 % | O | Elongation in 50 mm | ||
315 °C | 80 % Show Material materials with Elongation of 80 % | O | Elongation in 50 mm | ||
370 °C | 85 % Show Material materials with Elongation of 85 % | O | Elongation in 50 mm | ||
Fatigue strength | 34 MPa Show Material materials with Fatigue strength of 34 MPa | O | for 5x10⁸ cycles | ||
Hardness, Brinell | 23.0 [-] Show Material materials with Hardness, Brinell of 23.0 [-] | O | AA Standards | ||
23.0 [-] Show Material materials with Hardness, Brinell of 23.0 [-] | O | 500 kg load, 10 mm ball | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | O | |||
Shear modulus | 25.0 GPa Show Material materials with Shear modulus of 25.0 GPa | O | |||
26.0 GPa Show Material materials with Shear modulus of 26.0 GPa | O | ||||
Shear strength | 60.0 MPa Show Material materials with Shear strength of 60.0 MPa | O | |||
Tensile strength | -195 °C | 172 MPa Show Material materials with Tensile strength of 172 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 103 MPa Show Material materials with Tensile strength of 103 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
75.0 - 105.0 MPa Show Material materials with Tensile strength of 75.0 - 105.0 MPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B547 | |||
75.0 MPa Show Material materials with Tensile strength of 75.0 MPa | O | AA Standards, ASTM B483 | |||
88.0 MPa Show Material materials with Tensile strength of 88.0 MPa | O | ||||
90.0 MPa Show Material materials with Tensile strength of 90.0 MPa | O | AA Standards | |||
0 °C | 97 MPa Show Material materials with Tensile strength of 97 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
110.0 MPa Show Material materials with Tensile strength of 110.0 MPa | O | AA Standards, ASTM B316 | |||
24 °C | 90 MPa Show Material materials with Tensile strength of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 70 MPa Show Material materials with Tensile strength of 70 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 55 MPa Show Material materials with Tensile strength of 55 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 40 MPa Show Material materials with Tensile strength of 40 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 28 MPa Show Material materials with Tensile strength of 28 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 20 MPa Show Material materials with Tensile strength of 20 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 14 MPa Show Material materials with Tensile strength of 14 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Yield strength | -196 °C | 41 MPa Show Material materials with Yield strength of 41 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 38 MPa Show Material materials with Yield strength of 38 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 34 MPa Show Material materials with Yield strength of 34 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
20.0 MPa Show Material materials with Yield strength of 20.0 MPa | O | AA Standards, ASTM B211, ASTM B241 | RP02 | ||
25.0 MPa Show Material materials with Yield strength of 25.0 MPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | RP02 | ||
29.0 MPa Show Material materials with Yield strength of 29.0 MPa | O | ||||
34.0 MPa Show Material materials with Yield strength of 34.0 MPa | O | ||||
35.0 MPa Show Material materials with Yield strength of 35.0 MPa | O | AA Standards | RP02 | ||
24 °C | 34 MPa Show Material materials with Yield strength of 34 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 32 MPa Show Material materials with Yield strength of 32 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 29 MPa Show Material materials with Yield strength of 29 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 24 MPa Show Material materials with Yield strength of 24 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 18 MPa Show Material materials with Yield strength of 18 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 14 MPa Show Material materials with Yield strength of 14 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 11 MPa Show Material materials with Yield strength of 11 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | O | ||
2.66e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.66e-05 1/K | O | |||
20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
Melting point | 640.0 - 655.0 °C Show Material materials with Melting point of 640.0 - 655.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
640.0 °C Show Material materials with Melting point of 640.0 °C | O | |||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | O | ||
904.0 J/(kg·K) Show Material materials with Specific heat capacity of 904.0 J/(kg·K) | O | |||
Thermal conductivity | 218.0 - 222.0 W/(m·K) Show Material materials with Thermal conductivity of 218.0 - 222.0 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
220.0 W/(m·K) Show Material materials with Thermal conductivity of 220.0 W/(m·K) | O | |||
222.0 W/(m·K) Show Material materials with Thermal conductivity of 222.0 W/(m·K) | O |
Electrical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Electrical conductivity | 33000000.0 - 34000000.0 S/m Show Material materials with Electrical conductivity of 33000000.0 - 34000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
34000000 S/m Show Material materials with Electrical conductivity of 34000000 S/m | O | Typical value | ||
Electrical resistivity | 2.8999999999999998e-08 Ω·m Show Material materials with Electrical resistivity of 2.8999999999999998e-08 Ω·m | O | ||
2.94e-08 - 3.03e-08 Ω·m Show Material materials with Electrical resistivity of 2.94e-08 - 3.03e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
3e-08 Ω·m Show Material materials with Electrical resistivity of 3e-08 Ω·m | O | Typical value | ||
Specific Electrical conductivity | 59.0 % IACS Show Material materials with Specific Electrical conductivity of 59.0 % IACS | O | Typical/Derived value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 99.0 % Show Material materials with Aluminium of 99.0 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
99.0 - 100.0 % Show Material materials with Aluminium of 99.0 - 100.0 % | O | ||
Copper | 0.05 - 0.2 % Show Material materials with Copper of 0.05 - 0.2 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Iron | 1.0 % Show Material materials with Iron of 1.0 % | O | |
Manganese | 0.05 % Show Material materials with Manganese of 0.05 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Other | 0.15 % Show Material materials with Other of 0.15 % | O | |
Silicon | 1.0 % Show Material materials with Silicon of 1.0 % | O | |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
| Workability | general (condition): good (O, H12, H14), acceptable (H16), poor(H18) | |