General
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Density | 2.83 g/cm³ Show Material materials with Density of 2.83 g/cm³ | T6 | AA Standards, ASTM B211, BS EN 573-3, BS EN 755-2 | Bar |
3.1 g/cm³ Show Material materials with Density of 3.1 g/cm³ | T6 |
Mechanical
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | T6 | AA Standards, ASTM B211, BS EN 573-3, BS EN 755-2 | Bar | |
Elongation | 8.0 % Show Material materials with Elongation of 8.0 % | T6 | BS EN 573-3, BS EN 755-2 | Bar | |
8.6 % Show Material materials with Elongation of 8.6 % | T6 | ||||
9.0 % Show Material materials with Elongation of 9.0 % | T6 | AA Standards, ASTM B211 | A100 | ||
10.0 % Show Material materials with Elongation of 10.0 % | T6 | AA Standards, ASTM B211 | A50 | ||
Hardness, Brinell | 110.0 [-] Show Material materials with Hardness, Brinell of 110.0 [-] | T6 | BS EN 573-3, BS EN 755-2 | Bar | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 26.0 - 27.5 GPa Show Material materials with Shear modulus of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | |||
Tensile strength | 310.0 MPa Show Material materials with Tensile strength of 310.0 MPa | T6 | BS EN 573-3, BS EN 755-2 | Bar | |
370.0 MPa Show Material materials with Tensile strength of 370.0 MPa | T6 | AA Standards, ASTM B211 | |||
380.0 MPa Show Material materials with Tensile strength of 380.0 MPa | T6 | ||||
Yield strength | 230.0 MPa Show Material materials with Yield strength of 230.0 MPa | T6 | BS EN 573-3, BS EN 755-2 | Bar | RP02 |
270.0 MPa Show Material materials with Yield strength of 270.0 MPa | T6 | ||||
275.0 MPa Show Material materials with Yield strength of 275.0 MPa | T6 | AA Standards, ASTM B211 | RP02 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Coefficient of thermal expansion | 2.29e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.29e-05 1/K | T6 | BS EN 573-3, BS EN 755-2 | Bar | |
2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T6 | ||||
20 °C | 2.2899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.2899999999999998e-05 1/K | T6 | AA Standards, ASTM B211 | ||
100 °C | 2.2899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.2899999999999998e-05 1/K | T6 | AA Standards, ASTM B211 | ||
Melting point | 535.0 °C Show Material materials with Melting point of 535.0 °C | T6 | BS EN 573-3, BS EN 755-2 | Bar | |
540.0 - 645.0 °C Show Material materials with Melting point of 540.0 - 645.0 °C | T6 | AA Standards, ASTM B211 | |||
540.0 °C Show Material materials with Melting point of 540.0 °C | T6 | ||||
Specific heat capacity | 860.0 J/(kg·K) Show Material materials with Specific heat capacity of 860.0 J/(kg·K) | T6 | |||
Thermal conductivity | 151.0 - 172.0 W/(m·K) Show Material materials with Thermal conductivity of 151.0 - 172.0 W/(m·K) | T6 | AA Standards, ASTM B211 | ||
170.0 W/(m·K) Show Material materials with Thermal conductivity of 170.0 W/(m·K) | T6 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 23000000.0 - 26000000.0 S/m Show Material materials with Electrical conductivity of 23000000.0 - 26000000.0 S/m | T6 | AA Standards, ASTM B211 |
Electrical resistivity | 3.85e-08 - 4.35e-08 Ω·m Show Material materials with Electrical resistivity of 3.85e-08 - 4.35e-08 Ω·m | T6 | AA Standards, ASTM B211 |
Chemical properties
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Aluminium | 91.3 - 94.6 % Show Material materials with Aluminium of 91.3 - 94.6 % | T6 | |||
Bismuth | 0.2 - 0.6 % Show Material materials with Bismuth of 0.2 - 0.6 % | T6 | AA Standards, ASTM B211, BS EN 573-3, BS EN 755-2 | Bar | |
Copper | 5.0 - 6.0 % Show Material materials with Copper of 5.0 - 6.0 % | T6 | AA Standards, ASTM B211, BS EN 573-3, BS EN 755-2 | Bar | |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | T6 | AA Standards, ASTM B211 | ||
0.7 % Show Material materials with Iron of 0.7 % | T6 | BS EN 573-3, BS EN 755-2 | Bar | ||
Lead | 0.2 - 0.6 % Show Material materials with Lead of 0.2 - 0.6 % | T6 | AA Standards, ASTM B211 | ||
0.2 - 0.4 % Show Material materials with Lead of 0.2 - 0.4 % | T6 | BS EN 573-3, BS EN 755-2 | Bar | ||
Other | 0.15 % Show Material materials with Other of 0.15 % | T6 | BS EN 573-3, BS EN 755-2 | Bar | Total |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | T6 | AA Standards, ASTM B211, BS EN 573-3, BS EN 755-2 | Bar | |
Zinc | 0.3 % Show Material materials with Zinc of 0.3 % | T6 | AA Standards, ASTM B211, BS EN 573-3, BS EN 755-2 | Bar |
Technological properties
Property | ||
---|---|---|
Application areas | Appliance parts & trim, Automotive trim, Fasteners and fittings, Ordnance | |
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: Limited operational damage(T3, T4, T451), no damage during operation, limited damage during laboratory tests (T8), general: sufficient, in principle it should be protected | |
General machinability | General: very good | |
Soldering general | Fair | |
Welding | Alloy 2011 has extremely poor weldability and thus welding is not recommended. However, as it is used for machined parts there is rarely a need to weld this alloy. Gas: Poor; Arc: Poor; Resistance: Poor | |
Workability | general (condition): poor(T3), acceptable (T4, T451), d (T8) |