General
Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.83 g/cm³ Show Material materials with Density of 2.83 g/cm³ | T8 | AA Standards, ASTM B210, ASTM B211 |
2.83 g/cm³ Show Material materials with Density of 2.83 g/cm³ | T8 | ||
3.1 g/cm³ Show Material materials with Density of 3.1 g/cm³ | T8 |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Bending Fatigue Strength | 125.0 MPa Show Material materials with Bending Fatigue Strength of 125.0 MPa | T8 | AA Standards | |
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | T8 | AA Standards, ASTM B210, ASTM B211 | |
70 GPa Show Material materials with Elastic modulus of 70 GPa | T8 | |||
Elongation | 7.0 % Show Material materials with Elongation of 7.0 % | T8 | AA Standards, ASTM B210 | A100 |
8.0 % Show Material materials with Elongation of 8.0 % | T8 | AA Standards, ASTM B210 | A50 | |
9.0 % Show Material materials with Elongation of 9.0 % | T8 | AA Standards, ASTM B211 | A100 | |
9.9 % Show Material materials with Elongation of 9.9 % | T8 | |||
10.0 % Show Material materials with Elongation of 10.0 % | T8 | AA Standards | A100 | |
10.0 % Show Material materials with Elongation of 10.0 % | T8 | AA Standards, ASTM B211 | A50 | |
12 % Show Material materials with Elongation of 12 % | T8 | |||
Fatigue strength | 124 MPa Show Material materials with Fatigue strength of 124 MPa | T8 | for 5x10⁸ cycles | |
Hardness, Brinell | 100.0 [-] Show Material materials with Hardness, Brinell of 100.0 [-] | T8 | AA Standards | |
100.0 [-] Show Material materials with Hardness, Brinell of 100.0 [-] | T8 | 500 kg load, 10 mm ball | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Shear modulus | 26.0 GPa Show Material materials with Shear modulus of 26.0 GPa | T8 | ||
Shear strength | 241.0 MPa Show Material materials with Shear strength of 241.0 MPa | T8 | ||
Tensile strength | 370.0 MPa Show Material materials with Tensile strength of 370.0 MPa | T8 | AA Standards, ASTM B211 | |
400.0 MPa Show Material materials with Tensile strength of 400.0 MPa | T8 | AA Standards, ASTM B210 | ||
405.0 MPa Show Material materials with Tensile strength of 405.0 MPa | T8 | AA Standards | ||
405 MPa Show Material materials with Tensile strength of 405 MPa | T8 | |||
410.0 MPa Show Material materials with Tensile strength of 410.0 MPa | T8 | |||
Yield strength | 275.0 MPa Show Material materials with Yield strength of 275.0 MPa | T8 | AA Standards, ASTM B211 | RP02 |
310.0 MPa Show Material materials with Yield strength of 310.0 MPa | T8 | AA Standards | RP02 | |
310 MPa Show Material materials with Yield strength of 310 MPa | T8 | RP02 | ||
310.0 MPa Show Material materials with Yield strength of 310.0 MPa | T8 | |||
315.0 MPa Show Material materials with Yield strength of 315.0 MPa | T8 | AA Standards, ASTM B210 | RP02 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T8 | |||
20 °C | 2.2899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.2899999999999998e-05 1/K | T8 | AA Standards, ASTM B210, ASTM B211 | ||
100 °C | 2.2899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.2899999999999998e-05 1/K | T8 | AA Standards, ASTM B210, ASTM B211 | ||
Melting point | 540.0 - 645.0 °C Show Material materials with Melting point of 540.0 - 645.0 °C | T8 | AA Standards, ASTM B210, ASTM B211 | ||
540.0 °C Show Material materials with Melting point of 540.0 °C | T8 | ||||
Specific heat capacity | 860.0 J/(kg·K) Show Material materials with Specific heat capacity of 860.0 J/(kg·K) | T8 | |||
Thermal conductivity | 151.0 - 172.0 W/(m·K) Show Material materials with Thermal conductivity of 151.0 - 172.0 W/(m·K) | T8 | AA Standards, ASTM B210, ASTM B211 | ||
170.0 W/(m·K) Show Material materials with Thermal conductivity of 170.0 W/(m·K) | T8 | ||||
20 °C | 173 W/(m·K) Show Material materials with Thermal conductivity of 173 W/(m·K) | T8 | unstated value | ||
25 °C | 171.36 W/(m·K) Show Material materials with Thermal conductivity of 171.36 W/(m·K) | T8 | unstated value |
Electrical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Electrical conductivity | 23000000.0 - 26000000.0 S/m Show Material materials with Electrical conductivity of 23000000.0 - 26000000.0 S/m | T8 | AA Standards, ASTM B210, ASTM B211 | |
26000000 S/m Show Material materials with Electrical conductivity of 26000000 S/m | T8 | Typical/derived value | ||
Electrical resistivity | 3.7999999999999996e-08 Ω·m Show Material materials with Electrical resistivity of 3.7999999999999996e-08 Ω·m | T8 | Typical value | |
3.85e-08 - 4.35e-08 Ω·m Show Material materials with Electrical resistivity of 3.85e-08 - 4.35e-08 Ω·m | T8 | AA Standards, ASTM B210, ASTM B211 | ||
Specific Electrical conductivity | 45.0 % IACS Show Material materials with Specific Electrical conductivity of 45.0 % IACS | T8 | Typical value |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 91.3 - 94.6 % Show Material materials with Aluminium of 91.3 - 94.6 % | T8 | |
Bismuth | 0.2 - 0.6 % Show Material materials with Bismuth of 0.2 - 0.6 % | T8 | AA Standards, ASTM B210, ASTM B211 |
Copper | 5.0 - 6.0 % Show Material materials with Copper of 5.0 - 6.0 % | T8 | AA Standards, ASTM B210, ASTM B211 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | T8 | AA Standards, ASTM B210, ASTM B211 |
0.7 % Show Material materials with Iron of 0.7 % | T8 | ||
Lead | 0.2 - 0.6 % Show Material materials with Lead of 0.2 - 0.6 % | T8 | AA Standards, ASTM B210, ASTM B211 |
Other | 0.15 % Show Material materials with Other of 0.15 % | T8 | |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | T8 | AA Standards, ASTM B210, ASTM B211 |
Zinc | 0.3 % Show Material materials with Zinc of 0.3 % | T8 | AA Standards, ASTM B210, ASTM B211 |
Technological properties
Property | ||
---|---|---|
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: Limited operational damage(T3, T4, T451), no damage during operation, limited damage during laboratory tests (T8), general: sufficient, in principle it should be protected | |
General machinability | General: very good | |
Workability | general (condition): poor(T3), acceptable (T4, T451), d (T8) |