Properties
General
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 125.0 MPa Show Material materials with Bending Fatigue Strength of 125.0 MPa | T6 | AA Standards | ||
Elastic modulus | 73.0 GPa Show Material materials with Elastic modulus of 73.0 GPa | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | ||
73 GPa Show Material materials with Elastic modulus of 73 GPa | T6 | ||||
Elongation | -195 °C | 14 % Show Material materials with Elongation of 14 % | T6 | Elongation in 50 mm | |
-80 °C | 13 % Show Material materials with Elongation of 13 % | T6 | Elongation in 50 mm | ||
1.0 % Show Material materials with Elongation of 1.0 % | T6 | AA Standards, ASTM B209, ASTM B247 | A100 | ||
2.0 % Show Material materials with Elongation of 2.0 % | T6 | AA Standards, ASTM B247 | A100 | ||
2.0 % Show Material materials with Elongation of 2.0 % | T6 | AA Standards, ASTM B247 | A50 | ||
3.0 % Show Material materials with Elongation of 3.0 % | T6 | AA Standards, ASTM B209 | A100 | ||
3.0 % Show Material materials with Elongation of 3.0 % | T6 | AA Standards, ASTM B247 | A50 | ||
5.0 % Show Material materials with Elongation of 5.0 % | T6 | AA Standards, ASTM B209, ASTM B241, ASTM B247 | A100 | ||
5.8 % Show Material materials with Elongation of 5.8 % | T6 | ||||
6.0 % Show Material materials with Elongation of 6.0 % | T6 | AA Standards, ASTM B241, ASTM B247 | A100 | ||
6.0 % Show Material materials with Elongation of 6.0 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B247 | A50 | ||
7.0 % Show Material materials with Elongation of 7.0 % | T6 | AA Standards, ASTM B210, ASTM B211, ASTM B247 | A100 | ||
7.0 % Show Material materials with Elongation of 7.0 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B241, ASTM B247 | A50 | ||
8.0 % Show Material materials with Elongation of 8.0 % | T6 | AA Standards, ASTM B210, ASTM B211 | A50 | ||
11.0 % Show Material materials with Elongation of 11.0 % | T6 | AA Standards | A100 | ||
0 °C | 13 % Show Material materials with Elongation of 13 % | T6 | Elongation in 50 mm | ||
24 °C | 13 % Show Material materials with Elongation of 13 % | T6 | Elongation in 50 mm | ||
100 °C | 15 % Show Material materials with Elongation of 15 % | T6 | Elongation in 50 mm | ||
150 °C | 20 % Show Material materials with Elongation of 20 % | T6 | Elongation in 50 mm | ||
205 °C | 38 % Show Material materials with Elongation of 38 % | T6 | Elongation in 50 mm | ||
260 °C | 52 % Show Material materials with Elongation of 52 % | T6 | Elongation in 50 mm | ||
315 °C | 65 % Show Material materials with Elongation of 65 % | T6 | Elongation in 50 mm | ||
370 °C | 72 % Show Material materials with Elongation of 72 % | T6 | Elongation in 50 mm | ||
Fatigue strength | 125 MPa Show Material materials with Fatigue strength of 125 MPa | T6 | for 5x10⁸ cycles | ||
Hardness, Brinell | 135.0 [-] Show Material materials with Hardness, Brinell of 135.0 [-] | T6 | AA Standards | ||
135.0 [-] Show Material materials with Hardness, Brinell of 135.0 [-] | T6 | 500 kg load, 10 mm ball | |||
Hardness, Rockwell B | 80.0 - 86.0 [-] Show Material materials with Hardness, Rockwell B of 80.0 - 86.0 [-] | T6 | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 28.0 GPa Show Material materials with Shear modulus of 28.0 GPa | T6 | |||
Shear strength | 240.0 MPa Show Material materials with Shear strength of 240.0 MPa | T6 | |||
Tensile strength | -195 °C | 580 MPa Show Material materials with Tensile strength of 580 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 510 MPa Show Material materials with Tensile strength of 510 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
395.0 MPa Show Material materials with Tensile strength of 395.0 MPa | T6 | AA Standards, ASTM B247 | |||
400.0 MPa Show Material materials with Tensile strength of 400.0 MPa | T6 | AA Standards, ASTM B247 | |||
405.0 MPa Show Material materials with Tensile strength of 405.0 MPa | T6 | AA Standards, ASTM B209, ASTM B247 | |||
415.0 MPa Show Material materials with Tensile strength of 415.0 MPa | T6 | AA Standards, ASTM B241, ASTM B247 | |||
420.0 MPa Show Material materials with Tensile strength of 420.0 MPa | T6 | AA Standards, ASTM B247 | |||
425.0 MPa Show Material materials with Tensile strength of 425.0 MPa | T6 | AA Standards, ASTM B247 | |||
435.0 MPa Show Material materials with Tensile strength of 435.0 MPa | T6 | AA Standards, ASTM B209, ASTM B247 | |||
440.0 MPa Show Material materials with Tensile strength of 440.0 MPa | T6 | AA Standards, ASTM B209, ASTM B241, ASTM B247 | |||
450.0 MPa Show Material materials with Tensile strength of 450.0 MPa | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B247 | |||
455.0 MPa Show Material materials with Tensile strength of 455.0 MPa | T6 | AA Standards, ASTM B209 | |||
460.0 MPa Show Material materials with Tensile strength of 460.0 MPa | T6 | AA Standards, ASTM B209 | |||
470.0 MPa Show Material materials with Tensile strength of 470.0 MPa | T6 | AA Standards, ASTM B241 | |||
485.0 MPa Show Material materials with Tensile strength of 485.0 MPa | T6 | AA Standards | |||
490.0 MPa Show Material materials with Tensile strength of 490.0 MPa | T6 | ||||
0 °C | 495 MPa Show Material materials with Tensile strength of 495 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 483 MPa Show Material materials with Tensile strength of 483 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 435 MPa Show Material materials with Tensile strength of 435 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 275 MPa Show Material materials with Tensile strength of 275 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 110 MPa Show Material materials with Tensile strength of 110 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 66 MPa Show Material materials with Tensile strength of 66 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 45 MPa Show Material materials with Tensile strength of 45 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 30 MPa Show Material materials with Tensile strength of 30 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Yield strength | 350.0 MPa Show Material materials with Yield strength of 350.0 MPa | T6 | AA Standards, ASTM B247 | RP02 | |
360.0 MPa Show Material materials with Yield strength of 360.0 MPa | T6 | AA Standards, ASTM B247 | RP02 | ||
365.0 MPa Show Material materials with Yield strength of 365.0 MPa | T6 | AA Standards, ASTM B241, ASTM B247 | RP02 | ||
370.0 MPa Show Material materials with Yield strength of 370.0 MPa | T6 | AA Standards, ASTM B247 | RP02 | ||
380.0 MPa Show Material materials with Yield strength of 380.0 MPa | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B247 | RP02 | ||
385.0 MPa Show Material materials with Yield strength of 385.0 MPa | T6 | AA Standards, ASTM B247 | RP02 | ||
395.0 MPa Show Material materials with Yield strength of 395.0 MPa | T6 | AA Standards, ASTM B209 | RP02 | ||
400.0 MPa Show Material materials with Yield strength of 400.0 MPa | T6 | AA Standards, ASTM B209, ASTM B241 | RP02 | ||
405.0 MPa Show Material materials with Yield strength of 405.0 MPa | T6 | AA Standards, ASTM B209 | RP02 | ||
415.0 MPa Show Material materials with Yield strength of 415.0 MPa | T6 | AA Standards | RP02 | ||
420.0 MPa Show Material materials with Yield strength of 420.0 MPa | T6 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T6 | ||
20 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | |
100 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | |
Melting point | 505.0 - 635.0 °C Show Material materials with Melting point of 505.0 - 635.0 °C | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | |
510.0 °C Show Material materials with Melting point of 510.0 °C | T6 | |||
Specific heat capacity | 870.0 J/(kg·K) Show Material materials with Specific heat capacity of 870.0 J/(kg·K) | T6 | ||
Thermal conductivity | 134.0 - 193.0 W/(m·K) Show Material materials with Thermal conductivity of 134.0 - 193.0 W/(m·K) | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | |
150.0 W/(m·K) Show Material materials with Thermal conductivity of 150.0 W/(m·K) | T6 |
Electrical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Electrical conductivity | 20000000.0 - 29000000.0 S/m Show Material materials with Electrical conductivity of 20000000.0 - 29000000.0 S/m | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | |
23000000 S/m Show Material materials with Electrical conductivity of 23000000 S/m | T6 | Typical/derived value | ||
Electrical resistivity | 3.45e-08 - 5e-08 Ω·m Show Material materials with Electrical resistivity of 3.45e-08 - 5e-08 Ω·m | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | |
4.3e-08 Ω·m Show Material materials with Electrical resistivity of 4.3e-08 Ω·m | T6 | Typical value | ||
Specific Electrical conductivity | 40.0 % IACS Show Material materials with Specific Electrical conductivity of 40.0 % IACS | T6 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 90.4 - 95.0 % Show Material materials with Aluminium of 90.4 - 95.0 % | T6 | |
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
Copper | 3.9 - 5.0 % Show Material materials with Copper of 3.9 - 5.0 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
0.7 % Show Material materials with Iron of 0.7 % | T6 | ||
Magnesium | 0.2 - 0.8 % Show Material materials with Magnesium of 0.2 - 0.8 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
Manganese | 0.4 - 1.2 % Show Material materials with Manganese of 0.4 - 1.2 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
Other | 0.15 % Show Material materials with Other of 0.15 % | T6 | |
Silicon | 0.5 - 1.2 % Show Material materials with Silicon of 0.5 - 1.2 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
Zirconium | 0.2 % Show Material materials with Zirconium of 0.2 % | T6 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected | |
| General machinability | General: poor (O), good to acceptable | |
| Workability | general (condition): poor(T3, T4, T451), not suitable (T6, T651, T6510, T6511) | |