Properties
General
| Property | Value | Temperature |
|---|---|---|
Density | 7.9 g/cm³ Show Material materials with Density of 7.9 g/cm³ at 23.0 °C | 23.0 °C |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Elastic modulus | 200 GPa Show Material materials with Elastic modulus of 200 GPa at 23.0 °C | 23.0 °C | |
Elongation | 8.1 % Show Material materials with Elongation of 8.1 % at 23.0 °C | 23.0 °C | |
Poisson's ratio | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] at 23.0 °C | 23.0 °C | Typical for Austenitic Stainless Steel |
Shear modulus | 77 GPa Show Material materials with Shear modulus of 77 GPa at 23.0 °C | 23.0 °C | Typical for Austenitic Stainless Steel |
Tensile strength | 1190 MPa Show Material materials with Tensile strength of 1190 MPa at 23.0 °C | 23.0 °C | |
Yield strength | 870 MPa Show Material materials with Yield strength of 870 MPa at 23.0 °C | 23.0 °C |
Thermal
| Property | Value | Temperature |
|---|---|---|
Coefficient of thermal expansion | 1.6E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.6E-5 1/K at 23.0 °C | 23.0 °C |
Melting point | 1380 °C Show Material materials with Melting point of 1380 °C | |
Specific heat capacity | 490 J/(kg·K) Show Material materials with Specific heat capacity of 490 J/(kg·K) at 23.0 °C | 23.0 °C |
Thermal conductivity | 15 W/(m·K) Show Material materials with Thermal conductivity of 15 W/(m·K) at 23.0 °C | 23.0 °C |
Electrical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Electrical resistivity | 8.5E-7 Ω·m Show Material materials with Electrical resistivity of 8.5E-7 Ω·m at 23.0 °C | 23.0 °C | Typical for Austenitic Stainless Steel |
Chemical properties
| Property | ||
|---|---|---|
Carbon | 0 - 0.08 % | |
Chromium | 16 - 18.5 % | |
Iron | 62 - 72 % | |
Manganese | 0 - 2 % | |
Molybdenum | 2 - 3 % | |
Nickel | 10 - 14 % | |
Nitrogen | 0 - 0.1 % | |
Phosphorus | 0 - 0.05 % | |
Silicon | 0 - 1 % | |
Sulfur | 0 - 0.03 % |