General
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastic modulus | 73.0 GPa Show Material materials with Elastic modulus of 73.0 GPa | T652 | AA Standards, ASTM B247 | |
Elongation | 1.0 % Show Material materials with Elongation of 1.0 % | T652 | AA Standards, ASTM B247 | A100 |
1.5 % Show Material materials with Elongation of 1.5 % | T652 | |||
2.0 % Show Material materials with Elongation of 2.0 % | T652 | AA Standards, ASTM B247 | A50 | |
2.0 % Show Material materials with Elongation of 2.0 % | T652 | AA Standards, ASTM B247 | A100 | |
5.0 % Show Material materials with Elongation of 5.0 % | T652 | AA Standards, ASTM B247 | A100 | |
6.0 % Show Material materials with Elongation of 6.0 % | T652 | AA Standards, ASTM B247 | A50 | |
6.0 % Show Material materials with Elongation of 6.0 % | T652 | AA Standards, ASTM B247 | A100 | |
7.0 % Show Material materials with Elongation of 7.0 % | T652 | AA Standards, ASTM B247 | A100 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Shear modulus | 26.0 - 27.5 GPa Show Material materials with Shear modulus of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Tensile strength | 395.0 MPa Show Material materials with Tensile strength of 395.0 MPa | T652 | AA Standards, ASTM B247 | |
400.0 MPa Show Material materials with Tensile strength of 400.0 MPa | T652 | AA Standards, ASTM B247 | ||
405.0 MPa Show Material materials with Tensile strength of 405.0 MPa | T652 | AA Standards, ASTM B247 | ||
415.0 MPa Show Material materials with Tensile strength of 415.0 MPa | T652 | AA Standards, ASTM B247 | ||
420.0 MPa Show Material materials with Tensile strength of 420.0 MPa | T652 | AA Standards, ASTM B247 | ||
425.0 MPa Show Material materials with Tensile strength of 425.0 MPa | T652 | AA Standards, ASTM B247 | ||
435.0 MPa Show Material materials with Tensile strength of 435.0 MPa | T652 | AA Standards, ASTM B247 | ||
440.0 MPa Show Material materials with Tensile strength of 440.0 MPa | T652 | AA Standards, ASTM B247 | ||
450.0 MPa Show Material materials with Tensile strength of 450.0 MPa | T652 | AA Standards, ASTM B247 | ||
460.0 MPa Show Material materials with Tensile strength of 460.0 MPa | T652 | |||
Yield strength | 330.0 MPa Show Material materials with Yield strength of 330.0 MPa | T652 | AA Standards, ASTM B247 | RP02 |
340.0 MPa Show Material materials with Yield strength of 340.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
345.0 MPa Show Material materials with Yield strength of 345.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
350.0 MPa Show Material materials with Yield strength of 350.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
360.0 MPa Show Material materials with Yield strength of 360.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
365.0 MPa Show Material materials with Yield strength of 365.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
370.0 MPa Show Material materials with Yield strength of 370.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
380.0 MPa Show Material materials with Yield strength of 380.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
385.0 MPa Show Material materials with Yield strength of 385.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
390.0 MPa Show Material materials with Yield strength of 390.0 MPa | T652 |
Thermal
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T652 | ||
20 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T652 | AA Standards, ASTM B247 | |
100 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T652 | AA Standards, ASTM B247 | |
Melting point | 505.0 - 635.0 °C Show Material materials with Melting point of 505.0 - 635.0 °C | T652 | AA Standards, ASTM B247 | |
510.0 °C Show Material materials with Melting point of 510.0 °C | T652 | |||
Specific heat capacity | 870.0 J/(kg·K) Show Material materials with Specific heat capacity of 870.0 J/(kg·K) | T652 | ||
Thermal conductivity | 134.0 - 193.0 W/(m·K) Show Material materials with Thermal conductivity of 134.0 - 193.0 W/(m·K) | T652 | AA Standards, ASTM B247 | |
150.0 W/(m·K) Show Material materials with Thermal conductivity of 150.0 W/(m·K) | T652 |
Electrical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Electrical conductivity | 20000000.0 - 29000000.0 S/m Show Material materials with Electrical conductivity of 20000000.0 - 29000000.0 S/m | T652 | AA Standards, ASTM B247 | |
23000000 S/m Show Material materials with Electrical conductivity of 23000000 S/m | T652 | Typical/derived value | ||
Electrical resistivity | 3.45e-08 - 5e-08 Ω·m Show Material materials with Electrical resistivity of 3.45e-08 - 5e-08 Ω·m | T652 | AA Standards, ASTM B247 | |
4.3e-08 Ω·m Show Material materials with Electrical resistivity of 4.3e-08 Ω·m | T652 | Typical value | ||
Specific Electrical conductivity | 40.0 % IACS Show Material materials with Specific Electrical conductivity of 40.0 % IACS | T652 | Typical value |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 90.4 - 95.0 % Show Material materials with Aluminium of 90.4 - 95.0 % | T652 | |
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | T652 | AA Standards, ASTM B247 |
Copper | 3.9 - 5.0 % Show Material materials with Copper of 3.9 - 5.0 % | T652 | AA Standards, ASTM B247 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | T652 | AA Standards, ASTM B247 |
0.7 % Show Material materials with Iron of 0.7 % | T652 | ||
Magnesium | 0.2 - 0.8 % Show Material materials with Magnesium of 0.2 - 0.8 % | T652 | AA Standards, ASTM B247 |
Manganese | 0.4 - 1.2 % Show Material materials with Manganese of 0.4 - 1.2 % | T652 | AA Standards, ASTM B247 |
Other | 0.15 % Show Material materials with Other of 0.15 % | T652 | |
Silicon | 0.5 - 1.2 % Show Material materials with Silicon of 0.5 - 1.2 % | T652 | AA Standards, ASTM B247 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | T652 | AA Standards, ASTM B247 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T652 | AA Standards, ASTM B247 |
Zirconium | 0.2 % Show Material materials with Zirconium of 0.2 % | T652 |
Technological properties
Property | ||
---|---|---|
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected | |
General machinability | General: poor (O), good to acceptable | |
Workability | general (condition): poor(T3, T4, T451), not suitable (T6, T651, T6510, T6511) |