General
Property | Value | Testing Standard |
---|---|---|
Density | 1.63 g/cm³ Show Supplier Material materials with Density of 1.63 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Testing Standard | Comment |
---|---|---|---|---|
Elastic modulus | 14.6 GPa Show Supplier Material materials with Elastic modulus of 14.6 GPa | ISO 527-2/1A | 1mm/min | |
Elongation | 1.7 % Show Supplier Material materials with Elongation of 1.7 % | ISO 527-2/1A | 5mm/min | |
Flexural modulus | 14.1 GPa Show Supplier Material materials with Flexural modulus of 14.1 GPa | ISO 178 | 2mm/min | |
Flexural strength | 275 MPa Show Supplier Material materials with Flexural strength of 275 MPa | ISO 178 | 2mm/min | |
Impact strength, Charpy notched | 23 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23 °C | 40 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -40 °C | 11 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m² | ISO 180/1A | |
23 °C | 11 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m² | ISO 180/1A | ||
Tensile strength | 192 MPa Show Supplier Material materials with Tensile strength of 192 MPa | ISO 527-2/1A | 5mm/min |
Thermal
Property | Value | Testing Standard | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 1.6e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.6e-05 1/K | ISO 11359-1/-2 | 23°C-55°C | ||
4.6e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 4.6e-05 1/K | ISO 11359-1/-2 | 23°C-55°C, Transverse | |||
Heat deflection temperature | 265 °C Show Supplier Material materials with Heat deflection temperature of 265 °C | ISO 75/2Af | 1.80 MPa | ||
270 °C Show Supplier Material materials with Heat deflection temperature of 270 °C | ISO 75/2Bf | 0.45 MPa | |||
Melting point | 280 °C Show Supplier Material materials with Melting point of 280 °C | ISO 11357-1/-3 | 10°C/min | ||
Flammability | Thickness tested (mm): 0.8, Class: V-0, Standard: UL 94 |
Electrical
Property | Value | Testing Standard | Comment |
---|---|---|---|
Comparative tracking index | 150 V Show Supplier Material materials with Comparative tracking index of 150 V | IEC 60112 | Sol.A |
Rheological Properties
Property | Value | Testing Standard | Condition | Comment |
---|---|---|---|---|
Melt mass-flow rate | 124 g/10min Show Supplier Material materials with Melt mass-flow rate of 124 g/10min | ISO 1133 | 315°C/5Kg | |
Shrinkage | 0.1 % Show Supplier Material materials with Shrinkage of 0.1 % | ISO 294-4 | 330/140/50* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.6 % Show Supplier Material materials with Shrinkage of 0.6 % | ISO 294-4 | 330/140/50* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE | |
Color | Natural | |
Features | Flame Retardant, Heat Stabilized | |
Fillers | 40% Glass Fiber | |
Processing methods | Injection Molding |