RADIFLAM A RV350 AF 830 BR

Alternative and trade names
PA66-GF35 FR
Want to keep this datasheet? Save it now in your required format

Description

PA66 flame retardant injection moulding grade with red phosphorus. 35% glass fibre reinforced. Natural red brick colour.

Suitable for parts requiring fire retardancy along with high stiffness and good mechanical resistance. Rated V-0 at 0.75 mm according to UL-94.

This material data has been provided by Radici Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting StandardThickness

Density

1.47 g/cm³

Show Supplier Material materials with Density of 1.47 g/cm³

dry

ISO 1183

Moisture absorption

1.3 %

Show Supplier Material materials with Moisture absorption of 1.3 %

50% RH

ISO 62

2 mm

Water absorption

5.4 %

Show Supplier Material materials with Water absorption of 5.4 %

ISO 62

2 mm

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

9 GPa

Show Supplier Material materials with Elastic modulus of 9 GPa

50%RH

ISO 527-2/1A

1mm/min

11 GPa

Show Supplier Material materials with Elastic modulus of 11 GPa

dry

ISO 527-2/1A

1mm/min

Elongation

2 %

Show Supplier Material materials with Elongation of 2 %

dry

ISO 527-2/1A

5mm/min

3 %

Show Supplier Material materials with Elongation of 3 %

50%RH

ISO 527-2/1A

5mm/min

Flexural modulus

10 GPa

Show Supplier Material materials with Flexural modulus of 10 GPa

dry

ISO 178

2mm/min

Flexural strength

240 MPa

Show Supplier Material materials with Flexural strength of 240 MPa

dry

ISO 178

2mm/min

Impact strength, Charpy notched

-30 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²

dry

ISO 179/1eA

23 °C

14 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 14 kJ/m²

dry

ISO 179/1eA

23 °C

17 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 17 kJ/m²

50%RH

ISO 179/1eA

Impact strength, Charpy unnotched

-30 °C

65 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 65 kJ/m²

dry

ISO 179/1eU

23 °C

70 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 70 kJ/m²

dry

ISO 179/1eU

23 °C

75 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 75 kJ/m²

50%RH

ISO 179/1eU

Unlock all property charts

Tensile strength

105 MPa

Show Supplier Material materials with Tensile strength of 105 MPa

50%RH

ISO 527-2/1A

5mm/min

160 MPa

Show Supplier Material materials with Tensile strength of 160 MPa

dry

ISO 527-2/1A

5mm/min

Thermal

PropertyValueThicknessTesting StandardPressureComment

Glow Wire Flammability Index

960 °C

Show Supplier Material materials with Glow Wire Flammability Index of 960 °C

1 mm, 2 mm

IEC 60695-2-12

Glow Wire Ignition Temperature

725 °C

Show Supplier Material materials with Glow Wire Ignition Temperature of 725 °C

1 mm

IEC 60695-2-13

750 °C

Show Supplier Material materials with Glow Wire Ignition Temperature of 750 °C

2 mm

IEC 60695-2-12

Heat deflection temperature

235 °C

Show Supplier Material materials with Heat deflection temperature of 235 °C

ISO 75/2Af

2 MPa

250 °C

Show Supplier Material materials with Heat deflection temperature of 250 °C

ISO 75/2Bf

0.45 MPa

Melting point

260 °C

Show Supplier Material materials with Melting point of 260 °C

ISO 11357-1/-3

10°C/min

Vicat softening temperature

245 °C

Show Supplier Material materials with Vicat softening temperature of 245 °C

ISO 306

50°C/h 50N

Flammability

Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | Class: V-0 ,method: UL 94, and thickness tested (mm): 0.8

Electrical

PropertyValueConditionTesting StandardComment

Comparative tracking index

550 V

Show Supplier Material materials with Comparative tracking index of 550 V

dry

IEC 60112

Sol.A

Surface resistivity

1e+10 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq

50%RH

IEC 60093

500V

1e+12 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq

dry

IEC 60093

500V

Volume resistivity

1e+12 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+12 Ω·cm

50%RH

IEC 60093

500V

1e+14 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+14 Ω·cm

dry

IEC 60093

500V

Rheological Properties

PropertyValueConditionTesting StandardComment

Shrinkage

0.3 %

Show Supplier Material materials with Shrinkage of 0.3 %

dry

ISO 294-4

1 %

Show Supplier Material materials with Shrinkage of 1 %

dry

ISO 294-4

Transverse

Technological properties

Property
Certifications

RoHS 2011/65/UE

Color

Natural

Fillers

35% Glass Fiber

Processing methods

Injection Molding