RADITECK P RCM651K 1700NT

Alternative and trade names
PPS-(GF+MX)65
Want to keep this datasheet? Save it now in your required format

Description

PPS 65% glass fibre and mineral filler reinforced injection. Lubricated, easier processing. Heat stabilized. Natural colour.

Balanced matching of excellent chemical resistance, inherent flame retardancy and very good heat ageing properties retention. Suitable for parts requiring high stiffness and high mechanical strength, along with good dimensional stability and low warpage. Ease of processing thanks to good flowability.

This material data has been provided by Radici Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.93 g/cm³

Show Supplier Material materials with Density of 1.93 g/cm³

ISO 1183

Water absorption

ISO 62, thickness tested (mm): 2

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

23.15 GPa

Show Supplier Material materials with Elastic modulus of 23.15 GPa

ISO 527-2/1A, 1mm/min

Elongation

23.0 °C

0.7 %

Show Supplier Material materials with Elongation of 0.7 %

ISO 527-2/1A, 5mm/min

Flexural modulus

23.0 °C

23.5 GPa

Show Supplier Material materials with Flexural modulus of 23.5 GPa

ISO 178, 2mm/min

Flexural strength

23.0 °C

205 MPa

Show Supplier Material materials with Flexural strength of 205 MPa

ISO 178, 2mm/min

Impact strength, Charpy notched

23.0 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 5 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

23.0 °C

13 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 13 kJ/m²

ISO 179/1eU

Impact strength, Izod notched

23.0 °C

5.5 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 5.5 kJ/m²

ISO 180/1A

Tensile strength

23.0 °C

130 MPa

Show Supplier Material materials with Tensile strength of 130 MPa

ISO 527-2/1A, 5mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.77E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.77E-5 1/K

ISO 11359-1/-2, 23°C-55°C

Coefficient of thermal expansion, transverse

23.0 °C

3.15E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 3.15E-5 1/K

ISO 11359-1/-2, 23°C-55°C

Heat deflection temperature, 0.45 MPa

275 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 275 °C

ISO 75/2Bf

Heat deflection temperature, 1.80 MPa

260 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 260 °C

ISO 75/2Af

Melting point

280 °C

Show Supplier Material materials with Melting point of 280 °C

ISO 11357-1/-3, 10°C/min

Flammability

Class: V-0 ,method: UL 94, and thickness tested (mm): 0.8

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

150 V

Show Supplier Material materials with Comparative tracking index of 150 V

IEC 60112, Sol.A

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage of 0.6 %

ISO 294-4, normal

Shrinkage, transverse

23.0 °C

0.2 %

Show Supplier Material materials with Shrinkage, transverse of 0.2 %

ISO 294-4, parallel

Melt mass-flow rate

ISO 1133, 315°C/5Kg

Technological properties

Property
Certifications

RoHS 2011/65/UE

Color

Natural

Fillers

65% Glass Fiber and Mineral Powder

Processing methods

Injection Molding