RADILON MIXLOY S RVA150K 100 NT

Alternative and trade names
(PA6+ABS)-GF15
Want to keep this datasheet? Save it now in your required format

Description

PA6/ABS blend, 15% glass fibre injection moulding grade. Heat stabilized. Natural colour.

Suitable for parts requiring improved stiffness and low moisture absorption. Excellent aesthetic surface aspect.

This material data has been provided by Radici Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting StandardThickness

Density

1.18 g/cm³

Show Supplier Material materials with Density of 1.18 g/cm³

dry

ISO 1183

Moisture absorption

1.6 %

Show Supplier Material materials with Moisture absorption of 1.6 %

50% RH

ISO 62

2 mm

Water absorption

5.2 %

Show Supplier Material materials with Water absorption of 5.2 %

ISO 62

2 mm

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

4 GPa

Show Supplier Material materials with Elastic modulus of 4 GPa

50%RH

ISO 527-2/1A

1mm/min

5 GPa

Show Supplier Material materials with Elastic modulus of 5 GPa

dry

ISO 527-2/1A

1mm/min

Elongation

4 %

Show Supplier Material materials with Elongation of 4 %

dry

ISO 527-2/1A

50mm/min

11 %

Show Supplier Material materials with Elongation of 11 %

50%RH

ISO 527-2/1A

50mm/min

Elongation at yield

4 %

Show Supplier Material materials with Elongation at yield of 4 %

dry

ISO 527-2/1A

7 %

Show Supplier Material materials with Elongation at yield of 7 %

50%RH

ISO 527-2/1A

Flexural modulus

3 GPa

Show Supplier Material materials with Flexural modulus of 3 GPa

50%RH

ISO 178

2mm/min

5 GPa

Show Supplier Material materials with Flexural modulus of 5 GPa

dry

ISO 178

2mm/min

Flexural strength

95 MPa

Show Supplier Material materials with Flexural strength of 95 MPa

50%RH

ISO 178

2mm/min

150 MPa

Show Supplier Material materials with Flexural strength of 150 MPa

dry

ISO 178

2mm/min

Impact strength, Charpy notched

-30 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²

dry

ISO 179/1eA

23 °C

12 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m²

dry

ISO 179/1eA

Impact strength, Charpy unnotched

23 °C

67 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 67 kJ/m²

dry

ISO 179/1eU

23 °C

80 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 80 kJ/m²

50%RH

ISO 179/1eU

Unlock all property charts

Yield strength

65 MPa

Show Supplier Material materials with Yield strength of 65 MPa

50%RH

ISO 527-2/1A

50mm/min

100 MPa

Show Supplier Material materials with Yield strength of 100 MPa

dry

ISO 527-2/1A

50mm/min

Thermal

PropertyValueTesting StandardComment

Melting point

224 °C

Show Supplier Material materials with Melting point of 224 °C

ISO 11357-1/-3

10°C/min

Flammability

Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | Class: HB ,method: UL 94, and thickness tested (mm): 1.6

Technological properties

Property
Certifications

RoHS 2011/65/UE

Color

Natural

Fillers

15% Glass Fiber

Processing methods

Injection Molding