1.7225 QT EN and Peeled

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by Remy Stahl.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Dimension

PropertyValue

Dimensions

Round-Bar length: 36-120 mm

Mechanical

PropertyValueComment

Elongation

10 %

Show Supplier Material materials with Elongation of 10 %

min.

Tensile strength

650.0 - 1200.0 MPa

Show Supplier Material materials with Tensile strength of 650.0 - 1200.0 MPa

Yield strength

500.0 MPa

Show Supplier Material materials with Yield strength of 500.0 MPa

min., RP02

Chemical properties

PropertyValueComment

Carbon

0.38 - 0.45 %

Show Supplier Material materials with Carbon of 0.38 - 0.45 %

Chromium

0.9 - 1.2 %

Show Supplier Material materials with Chromium of 0.9 - 1.2 %

Manganese

0.6 - 0.99 %

Show Supplier Material materials with Manganese of 0.6 - 0.99 %

Molybdenum

0.15 - 0.3 %

Show Supplier Material materials with Molybdenum of 0.15 - 0.3 %

Phosphorus

0.025 %

Show Supplier Material materials with Phosphorus of 0.025 %

max.

Silicon

0.4 %

Show Supplier Material materials with Silicon of 0.4 %

max.

Sulfur

0.02 - 0.035 %

Show Supplier Material materials with Sulfur of 0.02 - 0.035 %

Technological properties

Property
Application areas

Connecting parts, Mechanical Engineering, Automotive engineering

Processing history

Quenched and Tempered and Pealed