Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.2 g/cm³ Show Supplier Material materials with Density of 1.2 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.11 % Show Supplier Material materials with Moisture absorption of 0.11 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.19 [-] Show Supplier Material materials with Relative density of 1.19 [-] | ASTM D 792 |
Water absorption | 23.0 °C | 0.13 % Show Supplier Material materials with Water absorption of 0.13 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.3 GPa Show Supplier Material materials with Elastic modulus of 2.3 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 73 % Show Supplier Material materials with Elongation of 73 % | ISO 527 | break, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.4 GPa Show Supplier Material materials with Flexural modulus of 2.4 GPa | ISO 178 | 2 mm/min | ||
Flexural strength | 23.0 °C | 96 MPa Show Supplier Material materials with Flexural strength of 96 MPa | ISO 178 | yield, 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 138 MPa Show Supplier Material materials with Hardness, Ball Indentation of 138 MPa | ISO 2039-1 | H358/30 | ||
Impact strength, Charpy notched | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, 23°C | ||
Impact strength, Izod notched | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 10 kJ/m² | ISO 180/1A | 80*10*3, 23°C | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 100 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 100 J/m | ASTM D 256 | ||
Instrumented Impact, Total Energy | 23.0 °C | 65 J Show Supplier Material materials with Instrumented Impact, Total Energy of 65 J | ASTM D 3763 | 23°C | ||
Tensile strength | 23.0 °C | 63 MPa Show Supplier Material materials with Tensile strength of 63 MPa | ISO 527 | yield, 50 mm/min | ||
Impact strength, Charpy unnotched | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C | ||||
Impact strength, Izod unnotched | ISO 180/1U | unnotched 80*10*3, -30°C | ||||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | Pass | IEC 60695-10-2 | 125°C +/- 2°C | |||
Coefficient of thermal expansion | 23.0 °C | 7.7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.7E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||||
Glow Wire Ignition Temperature | 850 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 850 °C | IEC 60695-2-13 | 3.0 mm | |||
Heat deflection temperature | 121 - 131 °C Show Supplier Material materials with Heat deflection temperature of 121 - 131 °C | ||||
Heat deflection temperature, 0.45 MPa | 131 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 131 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 121 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 121 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Relative temperature index, electrical | 130 °C Show Supplier Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 120 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | |||
Relative temperature index, mechanical strength | 130 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | |||
Vicat softening temperature | 146 °C Show Supplier Material materials with Vicat softening temperature of 146 °C | ISO 306 | Rate A/50 | |||
Flammability | UL Recognized, 94V-2 Flame Class Rating: ≥0.4mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.4mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> Glow Wire Ignitability Temperature, 1.5 mm: 850°C IEC 60695-2-13 <br> UV-light, water exposure/immersion: F1- UL 746C <br> Glow Wire Flammability Index, 1.5 mm: 960°C IEC 60695-2-12 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101088457- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 3 V Show Supplier Material materials with Comparative tracking index of 3 V | UL 746A | (UL) {PLC} |
Dielectric constant, 1GHz | 23.0 °C | 2.78 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 2.78 [-] | ASTM ES 7-83 | 1.1 GHz |
Dielectric constant, 1MHz | 23.0 °C | 2.7 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 2.7 [-] | IEC 62631-2-1 |
Dielectric constant, 60Hz | 23.0 °C | 2.4 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 2.4 [-] | IEC 62631-2-1 | 50/60 Hz |
Dielectric strength | 23.0 °C | 18 kV/mm Show Supplier Material materials with Dielectric strength of 18 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Dissipation factor, 1GHz | 23.0 °C | 5.6E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 5.6E-3 [-] | ASTM ES 7-83 | |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 50Hz | 23.0 °C | 1E-3 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 1E-3 [-] | IEC 62631-2-1 | 50/60 Hz |
High Amp Arc Ignition | 23.0 °C | 0.4 mm Show Supplier Material materials with High Amp Arc Ignition of 0.4 mm | ≥, UL 746A | PLC 1 |
Hot-Wire Ignition | 23.0 °C | 0.4 mm Show Supplier Material materials with Hot-Wire Ignition of 0.4 mm | ≥, UL 746A | PLC 3 |
Sheet resistivity, ROA | 23.0 °C | 1.00E+16 - 1.00E+17 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+16 - 1.00E+17 Ω | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+16 - 1.00E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+16 - 1.00E+17 Ω·cm | IEC 62631-3-1 |
Optical
Property | Value | Comment |
---|---|---|
Transmission | 91 % Show Supplier Material materials with Transmission of 91 % | >, ASTM D 1003 | 2.54 mm |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 18 g/10min Show Supplier Material materials with Melt mass-flow rate of 18 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Melt volume-flow rate | 17 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 17 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.55 % Show Supplier Material materials with Shrinkage of 0.55 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.6 % Show Supplier Material materials with Shrinkage, transverse of 0.6 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | LED Lighting, Non-LED Lighting | |
Availability | Europe,Asia,Americas | |
Processing methods | Screw Speed: 40 to 70.0rpm | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |