Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.17 g/cm³ Show Supplier Material materials with Density of 1.17 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.13 % Show Supplier Material materials with Moisture absorption of 0.13 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.2 [-] Show Supplier Material materials with Relative density of 1.2 [-] | ASTM D 792 | |
Specific volume | 23.0 °C | 0.85 cm³/g Show Supplier Material materials with Specific volume of 0.85 cm³/g | ASTM D 792 |
Water absorption | 23.0 °C | 0.27 % Show Supplier Material materials with Water absorption of 0.27 % | ISO 62-1 | (23°C/saturated) |
Mechanical
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.45 GPa Show Supplier Material materials with Elastic modulus of 2.45 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 7 % Show Supplier Material materials with Elongation of 7 % | ISO 527 | yield, 50 mm/min | ||
Erichson scratch depth | 23.0 °C | 14 µm Show Supplier Material materials with Erichson scratch depth of 14 µm | SABIC method | 6N | ||
Flexural modulus | 23.0 °C | 2.45 GPa Show Supplier Material materials with Flexural modulus of 2.45 GPa | ISO 178 | 2 mm/min | ||
Flexural strength | 23.0 °C | 108 MPa Show Supplier Material materials with Flexural strength of 108 MPa | ISO 178 | yield, 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 128 MPa Show Supplier Material materials with Hardness, Ball Indentation of 128 MPa | ISO 2039-1 | H358/30 | ||
Hardness, Pencil test | H | ASTM D 3363 | 1kgf | |||
Hardness, Rockwell L | 23.0 °C | 108 [-] Show Supplier Material materials with Hardness, Rockwell L of 108 [-] | ASTM D 785 | ||
Hardness, Rockwell M | 23.0 °C | 93 [-] Show Supplier Material materials with Hardness, Rockwell M of 93 [-] | ASTM D 785 | | ||
Impact strength, Charpy notched | 23.0 °C | 3 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 3 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C | ||
Impact strength, Charpy unnotched | 23.0 °C | 47 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 47 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C | ||
Impact strength, Izod notched | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m² | ISO 180/1A | 80*10*3, 23°C | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 30 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 30 J/m | ASTM D 256 | ||
Instrumented Impact, Total Energy | 23.0 °C | 30 J Show Supplier Material materials with Instrumented Impact, Total Energy of 30 J | ASTM D 3763 | 23°C | ||
Taber Abrasion | 23.0 °C | 10 mg/1000cy Show Supplier Material materials with Taber Abrasion of 10 mg/1000cy | SABIC method | CS-17, 1 kg | ||
Tensile strength | 23.0 °C | 60 MPa Show Supplier Material materials with Tensile strength of 60 MPa | ISO 527 | break, 50 mm/min | ||
Impact strength, Izod unnotched | ISO 180/1U | 80*10*3, 23°C | ||||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C | ||||
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |||
Ball pressure temperature | 140 °C Show Supplier Material materials with Ball pressure temperature of 140 °C | IEC 60695-10-2 | approximate maximum | |||
Coefficient of thermal expansion | 23.0 °C | 7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||||
Glow Wire Ignition Temperature | 825 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 825 °C | IEC 60695-2-13 | 3.0 mm | |||
Heat deflection temperature, 0.45 MPa | 131 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 131 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 118 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 118 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Specific heat capacity | 23.0 °C | 1.4E-3 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 1.4E-3 J/(kg·K) | ASTM C 351 | ||
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.2 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 140 °C Show Supplier Material materials with Vicat softening temperature of 140 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Yellow Card Link: br UL Recognized, 94HB Flame Class Rating: 0.6 mm UL 94 br Glow Wire Ignitability Temperature, 1.0 mm: 850 °C IEC 60695-2-13 br Glow Wire Flammability Index, 1.0 mm: 900 °C IEC 60695-2-12 | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 2 V Show Supplier Material materials with Comparative tracking index of 2 V | UL 746A | (UL) {PLC} |
Optical
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 14.5 g/10min Show Supplier Material materials with Melt mass-flow rate of 14.5 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Melt volume-flow rate | 13 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 13 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Medical Device, Motorcycle, Non-LED Lighting, Personal Computing, Wiring Devices, Wireless Communications, Cluster, City, Auto Aftermarket, Audio, Building Accessory, Air Conditioning, Fluid Delivery, Enclosures, Electronic Components | |
| Availability | Asia | |
| Features | UV Resistant | |
| Processing methods | Drying Temperature: 120 °C br Drying Time: 3 to 4.0 hrs br Maximum Moisture Content: 0.02 % br Melt Temperature: 295 to 315.0 °C br Nozzle Temperature: 290 to 310.0 °C br Front | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |