Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.51 g/cm³ Show Supplier Material materials with Density of 1.51 g/cm³ | ISO 1183 |
Limiting oxygen index | 23.0 °C | 50 % Show Supplier Material materials with Limiting oxygen index of 50 % | |
Moisture absorption | 23.0 °C | 0.5 % Show Supplier Material materials with Moisture absorption of 0.5 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.51 [-] Show Supplier Material materials with Relative density of 1.51 [-] | ASTM D 792 |
Water absorption | 23.0 °C | 0.9 % Show Supplier Material materials with Water absorption of 0.9 % | ASTM D 570 | (23°C/Saturated) |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 9.3 GPa Show Supplier Material materials with Elastic modulus of 9.3 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 3 % Show Supplier Material materials with Elongation of 3 % | ASTM D 638 | brk, Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 8.96 GPa Show Supplier Material materials with Flexural modulus of 8.96 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Flexural strength | 23.0 °C | 227 MPa Show Supplier Material materials with Flexural strength of 227 MPa | ASTM D 790 | brk, 2.6 mm/min, 100 mm span |
Hardness, Ball Indentation | 23.0 °C | 165 MPa Show Supplier Material materials with Hardness, Ball Indentation of 165 MPa | ISO 2039-1 | H358/30 |
Hardness, Rockwell M | 23.0 °C | 114 [-] Show Supplier Material materials with Hardness, Rockwell M of 114 [-] | ASTM D 785 | |
Impact strength, Charpy notched | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/2C | 23°C |
Impact strength, Charpy unnotched | 23.0 °C | 40 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C |
Impact strength, Izod notched | 23.0 °C | 85 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 85 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 85 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 85 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 40 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 40 kJ/m² | ISO 180/1U | unnotched 80*10*4, -30°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 427 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 427 J/m | ASTM D 4812 | 23°C |
Taber Abrasion | 23.0 °C | 20 mg/1000cy Show Supplier Material materials with Taber Abrasion of 20 mg/1000cy | SABIC method | CS-17, 1 kg |
Tensile strength | 23.0 °C | 168 MPa Show Supplier Material materials with Tensile strength of 168 MPa | ASTM D 638 | yld, Type I, 5 mm/min |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |||
Coefficient of thermal expansion | 23.0 °C | 1.98E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.98E-5 1/K | ASTM E 831 | -20°C to 150°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||||
Glow Wire Ignition Temperature | 900 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 900 °C | IEC 60695-2-13 | 2.0 mm | |||
Heat deflection temperature, 0.45 MPa | 212 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 212 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 210 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 210 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Relative temperature index, electrical | 180 °C Show Supplier Material materials with Relative temperature index, electrical of 180 °C | UL 746B | |||
Relative temperature index, mechanical impact | 170 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C | UL 746B | |||
Relative temperature index, mechanical strength | 180 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 180 °C | UL 746B | |||
Thermal conductivity | 23.0 °C | 0.29 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.29 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 227 °C Show Supplier Material materials with Vicat softening temperature of 227 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | NBS Smoke Density, Flaming, Ds 4 min: 1.6 | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 4 V Show Supplier Material materials with Comparative tracking index of 4 V | UL 746A | (UL) {PLC} |
Dielectric constant, 1MHz | 23.0 °C | 3.4 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 3.4 [-] | IEC 60250 |
Dielectric constant, 60Hz | 23.0 °C | 3.3 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 3.3 [-] | IEC 60250 | 50/60 Hz |
Dielectric strength | 23.0 °C | 24.8 kV/mm Show Supplier Material materials with Dielectric strength of 24.8 kV/mm | ASTM D 149 | in air, 1.6 mm |
Dissipation factor | 23.0 °C | 5.3E-3 [-] Show Supplier Material materials with Dissipation factor of 5.3E-3 [-] | ASTM D 150 | 2450 MHz |
Dissipation factor, 1MHz | 23.0 °C | 2.3E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 2.3E-3 [-] | IEC 60250 |
Dissipation factor, 1kHz | 23.0 °C | 1.5E-3 [-] Show Supplier Material materials with Dissipation factor, 1kHz of 1.5E-3 [-] | ASTM D 150 |
Dissipation factor, 50Hz | 23.0 °C | 1.6E-3 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 1.6E-3 [-] | IEC 60250 | 50/60 Hz |
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | UL 746A | PLC 4 |
High Volt Arc Track Rate | 23.0 °C | 3 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 3 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | UL 746A | PLC 1 |
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | IEC 60093 |
Volume resistivity | 23.0 °C | 3.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 3.00E+16 Ω·cm | ASTM D 257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 5 g/10min Show Supplier Material materials with Melt mass-flow rate of 5 g/10min | ASTM D 1238 | 337°C/6.6 kgf | |
Melt volume-flow rate | 6 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 6 cm³/10min | ISO 1133 | MVR at 360°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.2 % Show Supplier Material materials with Shrinkage of 0.2 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.2 % Show Supplier Material materials with Shrinkage, transverse of 0.2 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components, Enclosure/Housing/Cover, Electronics, Enclosures, Furnace/Heater, Fluid Delivery, Gear/Bearing/Slider, Heavy Vehicles, Lab Ware and Clinical Diagnostics, Individual Equiptment, Circuit Protection, Auto Electrical, Auto Aftermarket, Aircraft Exteriors, Animal Testing, Air Conditioning, Aerospace, Aircraft Seating, Air Intake System, Air Cabin Interiors, Defense Vehicles, Document Handling, Data Transfer, Data Management, Building/Construction Sheet, Wiring Devices, Weapon, Wireless Communications, Underhood, Vacuum Cleaner, Plumbing, Pharmaceutical Packaging & Drug Delivery, Power Boat, Pipe/Fitting, Pump, Refrigerator, Security/Detection, Semiconductor, Sail Boat, Sanitary, Surgical Devices, Personal Computing, Non-LED Lighting, Oil/Gas, Motorcycle, Navigation Unit, LED Lighting, Medical Device, Meter Gas, Infrastructure, Interior Rail Components | |
| Availability | Europe,Asia,Americas | |
| Features | High Stiffness, Hydrolytic Stability, Chemical Resistance, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Good metal adhesion, Amorphous, High Strength, General Purpose, High Heat Resistance, Good dimensional stability, Flame Retardant | |
| Processing methods | Rear | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |