ULTEM™ Resin 1110 - Asia

Want to keep this datasheet? Save it now in your required format

Description

Enhanced flow Polyetherimide (Tg 217C). ECO Conforming.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.7 GPa

Show Supplier Material materials with Elastic modulus of 3.7 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

70 %

Show Supplier Material materials with Elongation of 70 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

3.7 GPa

Show Supplier Material materials with Flexural modulus of 3.7 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

165 MPa

Show Supplier Material materials with Flexural strength of 165 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Tensile strength

23.0 °C

110 MPa

Show Supplier Material materials with Tensile strength of 110 MPa

ASTM D 638 | yld, Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature

198 °C

Show Supplier Material materials with Heat deflection temperature of 198 °C

Heat deflection temperature, 1.80 MPa

198 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 198 °C

ASTM D 648 | 6.4 mm, unannealed

Relative temperature index, electrical

170 °C

Show Supplier Material materials with Relative temperature index, electrical of 170 °C

UL 746B

Relative temperature index, mechanical impact

170 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C

UL 746B

Relative temperature index, mechanical strength

170 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 170 °C

UL 746B

Flammability

UL Recognized, 94-5VA Flame Class Rating: ≥3mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.75mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101048292- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

4 V

Show Supplier Material materials with Comparative tracking index of 4 V

UL 746A | (UL) {PLC}

High Amp Arc Ignition

23.0 °C

3 mm

Show Supplier Material materials with High Amp Arc Ignition of 3 mm

≥, UL 746A | PLC 3

High Volt Arc Track Rate

23.0 °C

2 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 2 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

3 mm

Show Supplier Material materials with Hot-Wire Ignition of 3 mm

≥, UL 746A | PLC 1

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Surgical Devices, Air Cabin Interiors

Availability

Europe,Asia,Americas

Processing methods

Front - Zone 3 Temperature: 345 to 400.0°C
Middle - Zone 2 Temperature: 340 to 400.0°C
Mold Temperature: 135 to 165.0°C
Melt Temperature: 350 to 400.0°C
Back Pressure: 0.3 to 0.7MPa
Rear - Zone 1 Temperature: 330 to 400.0°C
Vent Depth: 0.025 to 0.076mm
Maximum Moisture Content: 0.02%
Nozzle Temperature: 345 to 400.0°C
Shot to Cylinder Size: 40 to 60.0%
Screw Speed: 40 to 70.0rpm
Drying Temperature: 150°C
Drying Time: 4 to 6.0hrs
Drying Time (Cumulative): 24hrs

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.