NORYL™ Resin EM7301F - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ EM7301F resin is a 10% glass reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade exhibits high heat resistance, good flow and polyurethane foam adhesion along with creep resistance, dimensional stability, and hydrolytic stability. NORYL EM7301F resin is an excellent candidate for automotive interior applications such as audio speaker components. This material is available only in black.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

3 %

Show Supplier Material materials with Elongation of 3 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

3.5 GPa

Show Supplier Material materials with Flexural modulus of 3.5 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

90 MPa

Show Supplier Material materials with Flexural strength of 90 MPa

ISO 178 | break, 2 mm/min

Tensile strength

23.0 °C

60 MPa

Show Supplier Material materials with Tensile strength of 60 MPa

ISO 527 | break, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

115 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 115 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Technological properties

Property
Application areas

Electronic Components, Enclosures, Auto Aftermarket, Audio

Availability

Americas

Features

Hydrolytic Stability, Good Stiffness

Processing methods

Melt Temperature: 280 to 300.0°C
Front - Zone 3 Temperature: 280 to 300.0°C
Drying Temperature: 100 to 120.0°C
Rear - Zone 1 Temperature: 240 to 260.0°C
Nozzle Temperature: 260 to 280.0°C
Middle - Zone 2 Temperature: 260 to 280.0°C
Drying Time: 2 to 3.0hrs
Mold Temperature: 80 to 120.0°C
Hopper Temperature: 60 to 80.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.