NORYL GTX™ Resin GTX918W - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL GTX™ 918W resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high heat resistance, excellent chemical resistance, and high melt flow. NORYL GTX918W resin may be an excellent candidate for automotive under-the-hood and electrical applications requiring the retention of properties while under thermal load.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

30 %

Show Supplier Material materials with Elongation of 30 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

2.2 GPa

Show Supplier Material materials with Flexural modulus of 2.2 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

85 MPa

Show Supplier Material materials with Flexural strength of 85 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Izod notched

23.0 °C

20 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 20 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Tensile strength

23.0 °C

55 MPa

Show Supplier Material materials with Tensile strength of 55 MPa

ISO 527 | break, 50 mm/min

Thermal

PropertyValueComment

Heat deflection temperature

185 °C

Show Supplier Material materials with Heat deflection temperature of 185 °C

Heat deflection temperature, 0.45 MPa

185 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 185 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

1.3 %

Show Supplier Material materials with Shrinkage of 1.3 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Electronic Components, Console, Cooking Range, Auto Electrical, Circuit Protection, Meter Gas

Availability

Europe,Asia,Americas

Features

Hydrolytic Stability, Low Creep Sensitivity, Good Stiffness, Low Warpage, High Flow, Good Processability, Structural

Processing methods

Melt Temperature: 280 to 310.0°C
Middle - Zone 2 Temperature: 270 to 290.0°C
Drying Temperature: 100 to 120.0°C
Drying Time: 2 to 3.0hrs
Hopper Temperature: 60 to 80.0°C
Maximum Moisture Content: 0.07%
Nozzle Temperature: 270 to 300.0°C
Front - Zone 3 Temperature: 280 to 300.0°C
Rear - Zone 1 Temperature: 260 to 280.0°C
Mold Temperature: 80 to 120.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.