General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.3 g/cm³ Show Supplier Material materials with Density of 1.3 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 9.5 GPa Show Supplier Material materials with Elastic modulus of 9.5 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2.4 % Show Supplier Material materials with Elongation of 2.4 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 8.4 GPa Show Supplier Material materials with Flexural modulus of 8.4 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 200 MPa Show Supplier Material materials with Flexural strength of 200 MPa | ISO 178 | break, 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Impact strength, Charpy unnotched | 23.0 °C | 50 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 50 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C |
Impact strength, Izod notched | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 12 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 85 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 85 J/m | ASTM D 256 | notched, -30°C |
Impact strength, Izod unnotched | 23.0 °C | 45 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 45 kJ/m² | ISO 180/1U | unnotched 80*10*4, -30°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 550 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 550 J/m | ASTM D 4812 | unnotched, -30°C |
Tensile strength | 23.0 °C | 131 MPa Show Supplier Material materials with Tensile strength of 131 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Value | Comment | |
---|---|---|---|
Glow Wire Flammability Index | 775 °C Show Supplier Material materials with Glow Wire Flammability Index of 775 °C | ||
Glow Wire Ignition Temperature | 800 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 800 °C | IEC 60695-2-13 | 3.0 mm | |
Heat deflection temperature | 149 - 155 °C Show Supplier Material materials with Heat deflection temperature of 149 - 155 °C | ||
Heat deflection temperature, 0.45 MPa | 155 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 155 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |
Heat deflection temperature, 1.80 MPa | 149 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 149 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |
Vicat softening temperature | 167 °C Show Supplier Material materials with Vicat softening temperature of 167 °C | ISO 306 | Rate A/120 | |
Flammability | Glow Wire Ignitability Temperature, 1.5 mm: 825°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.5 mm: 825°C IEC 60695-2-12 |
Rheological Properties
Property | Value | Comment |
---|---|---|
Melt mass-flow rate | 30 g/10min Show Supplier Material materials with Melt mass-flow rate of 30 g/10min | ASTM D 1238 | 300°C/10 kgf |
Melt volume-flow rate | 26 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 26 cm³/10min | ISO 1133 | MVR at 300°C/10.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Hydroblocks | |
Availability | Europe | |
Processing methods | Drying Temperature: 100 to 120.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |