LNP™ THERMOCOMP™ Compound QF007 - Americas

Want to keep this datasheet? Save it now in your required format


LNP THERMOCOMP QF007 is a compound based on Nylon 6/10 resin containing 35% Glass Fiber.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts





23.0 °C

1.33 g/cm³

Show Supplier Material materials with Density of 1.33 g/cm³

ASTM D 792

Moisture absorption

23.0 °C

0.37 %

Show Supplier Material materials with Moisture absorption of 0.37 %

ISO 62 | (23°C / 50% RH)



Flexural modulus

23.0 °C

7.93 GPa

Show Supplier Material materials with Flexural modulus of 7.93 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

227 MPa

Show Supplier Material materials with Flexural strength of 227 MPa

ISO 178

Impact strength, Izod notched

23.0 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

130 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 130 J/m

ASTM D 256 | notched, 23°C

Tensile strength

23.0 °C

157 MPa

Show Supplier Material materials with Tensile strength of 157 MPa

ISO 527 | yield, 5 mm/min

Technological properties




High Stiffness, Structural

Processing methods

Melt Temperature: 270 to 275.0°C
Front - Zone 3 Temperature: 270 to 280.0°C
Middle - Zone 2 Temperature: 260 to 270.0°C
Back Pressure: 0.2 to 0.3MPa
Mold Temperature: 80 to 95.0°C
Maximum Moisture Content: 0.12 to 0.2%
Drying Time: 4hrs
Rear - Zone 1 Temperature: 250 to 260.0°C
Drying Temperature: 80°C
Screw Speed: 30 to 60.0rpm

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.