ULTEM™ Resin 9075 - Asia

Want to keep this datasheet? Save it now in your required format

Description

High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.3 GPa

Show Supplier Material materials with Elastic modulus of 3.3 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

85 %

Show Supplier Material materials with Elongation of 85 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

3.2 GPa

Show Supplier Material materials with Flexural modulus of 3.2 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

144 MPa

Show Supplier Material materials with Flexural strength of 144 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Impact strength, Izod notched

23.0 °C

69 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 69 kJ/m²

ASTM D 256 | notched, 23°C

Tensile strength

23.0 °C

96 MPa

Show Supplier Material materials with Tensile strength of 96 MPa

ASTM D 638 | yld, Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature

188 °C

Show Supplier Material materials with Heat deflection temperature of 188 °C

Heat deflection temperature, 1.80 MPa

188 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 188 °C

ASTM D 648 | 6.4 mm, unannealed

Flammability

Vertical Burn b (12s) passes at: 0sec FAR 25.853 <br> Vertical Burn a (60s) passes at: 1sec FAR 25.853 <br> FAA Flammability, FAR 25.853 A/B: SECT A-1- FAR 25.853

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Air Cabin Interiors, Aircraft Seating, Aerospace, Defense Vehicles, Infrastructure

Availability

Europe,Asia,Americas

Processing methods

Adapter Temperature: 285 to 335.0°C
Front - Zone 3 Temperature: 350 to 370.0°C
Calibrator Temperature: 140 to 170.0°C
Hopper Temperature: 80 to 100.0°C
Barrel - Zone 4 Temperature: 310 to 335.0°C
Drying Time: 4 to 6.0hrs
Vent Depth: 0.025 to 0.076mm
Melt Temperature: 350 to 370.0°C
Shot to Cylinder Size: 40 to 60.0%
Drying Time: 4 to 6.0hrs
Barrel - Zone 2 Temperature: 295 to 320.0°C
Die Temperature: 275 to 330.0°C
Nozzle Temperature: 350 to 370.0°C
Back Pressure: 0.3 to 0.7MPa
Maximum Moisture Content: 0.02%
Middle - Zone 2 Temperature: 345 to 365.0°C
Rear - Zone 1 Temperature: 340 to 360.0°C
Calibrator 2 Temperature: 90 to 130.0°C
Mold Temperature: 135 to 165.0°C
Maximum Moisture Content: 0.02%
Drying Time (Cumulative): 10hrs
Barrel - Zone 1 Temperature: 280 to 300.0°C
Screw Speed: 40 to 70.0rpm
Melt Temperature: 295 to 330.0°C
Barrel - Zone 3 Temperature: 305 to 330.0°C
Drying Temperature: 130 to 140.0°C
Drying Temperature: 135 to 145.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.