ULTEM™ Resin 9075 - Europe

Want to keep this datasheet? Save it now in your required format

Description

High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.2 GPa

Show Supplier Material materials with Elastic modulus of 3.2 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

6 %

Show Supplier Material materials with Elongation of 6 %

ISO 527 | yield, 50 mm/min

Flexural modulus

23.0 °C

3.2 GPa

Show Supplier Material materials with Flexural modulus of 3.2 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

120 MPa

Show Supplier Material materials with Flexural strength of 120 MPa

ISO 178 | break, 2 mm/min

Impact strength, Izod notched

23.0 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A | 80*10*4, -30°C

Tensile strength

23.0 °C

90 MPa

Show Supplier Material materials with Tensile strength of 90 MPa

ISO 527 | yield, 50 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

185 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 185 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Flammability

OSU peak heat release rate (5 minute test): 16kW/m² FAR 25.853 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> UL Compliant, 94V-0 Flame Class Rating: 1.6mm UL 94 by SABIC-IP

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage of 0.6 %

SABIC method | on tensile bar

Technological properties

Property
Application areas

Air Cabin Interiors, Aircraft Seating, Aerospace, Defense Vehicles, Infrastructure

Availability

Europe,Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, High Heat Resistance, Good dimensional stability, Flame Retardant

Processing methods

Drying Time: 4 to 6.0hrs
Barrel - Zone 1 Temperature: 280 to 300.0°C
Barrel - Zone 4 Temperature: 310 to 335.0°C
Hopper Temperature: 80 to 120.0°C
Calibrator Temperature: 140 to 170.0°C
Melt Temperature: 295 to 330.0°C
Melt Temperature: 350 to 370.0°C
Rear - Zone 1 Temperature: 340 to 360.0°C
Drying Temperature: 130 to 140.0°C
Barrel - Zone 2 Temperature: 295 to 320.0°C
Maximum Moisture Content: 0.02%
Front - Zone 3 Temperature: 350 to 370.0°C
Hopper Temperature: 80 to 100.0°C
Calibrator 2 Temperature: 90 to 130.0°C
Maximum Moisture Content: 0.02%
Barrel - Zone 3 Temperature: 305 to 330.0°C
Mold Temperature: 135 to 165.0°C
Middle - Zone 2 Temperature: 345 to 365.0°C
Drying Time: 4 to 6.0hrs
Nozzle Temperature: 350 to 370.0°C
Adapter Temperature: 285 to 335.0°C
Die Temperature: 275 to 330.0°C
Drying Temperature: 135 to 145.0°C
Back Pressure: 0.3 to 0.7MPa
Screw Speed: 40 to 70.0rpm
Shot to Cylinder Size: 40 to 60.0%
Vent Depth: 0.025 to 0.076mm

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.