Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 2.7 g/cm³ Show Supplier Material materials with Density of 2.7 g/cm³ |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 23.0 °C | 69 GPa Show Supplier Material materials with Elastic modulus of 69 GPa |
Elongation A5 | 23.0 °C | 12 % Show Supplier Material materials with Elongation A5 of 12 % |
Hardness, Brinell | 23.0 °C | 70 [-] Show Supplier Material materials with Hardness, Brinell of 70 [-] |
Tensile strength | 23.0 °C | 215 MPa Show Supplier Material materials with Tensile strength of 215 MPa |
Yield strength Rp0.2 | 23.0 °C | 160 MPa Show Supplier Material materials with Yield strength Rp0.2 of 160 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.34E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.34E-5 1/K |
Thermal conductivity | 23.0 °C | 200 W/(m·K) Show Supplier Material materials with Thermal conductivity of 200 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 23.0 °C | 3.00E+7 S/m Show Supplier Material materials with Electrical conductivity of 3.00E+7 S/m |
Chemical properties
Property | Value | Comment | |
---|---|---|---|
Aluminium | Balance | ||
Chromium | 0.05 % Show Supplier Material materials with Chromium of 0.05 % | ||
Copper | 0.1 % Show Supplier Material materials with Copper of 0.1 % | ||
Iron | 0.1 - 0.3 % Show Supplier Material materials with Iron of 0.1 - 0.3 % | ||
Magnesium | 0.35 - 0.6 % Show Supplier Material materials with Magnesium of 0.35 - 0.6 % | ||
Manganese | 0.1 % Show Supplier Material materials with Manganese of 0.1 % | ||
Other | 0.15 % Show Supplier Material materials with Other of 0.15 % | total, each 0.05 | |
Silicon | 0.3 - 0.6 % Show Supplier Material materials with Silicon of 0.3 - 0.6 % | ||
Titanium | 0.1 % Show Supplier Material materials with Titanium of 0.1 % | ||
Zinc | 0.15 % Show Supplier Material materials with Zinc of 0.15 % |