General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.66 g/cm³ Show Supplier Material materials with Density of 1.66 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.02 % Show Supplier Material materials with Water absorption of 0.02 % | ISO 62 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 1.8 % Show Supplier Material materials with Elongation of 1.8 % | ISO 527 |
Flexural modulus | 23.0 °C | 15 GPa Show Supplier Material materials with Flexural modulus of 15 GPa | ISO 178 |
Flexural strength | 23.0 °C | 280 MPa Show Supplier Material materials with Flexural strength of 280 MPa | ISO 178 |
Impact strength, Charpy notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179 |
Tensile strength | 23.0 °C | 190 MPa Show Supplier Material materials with Tensile strength of 190 MPa | ISO 527 |
Thermal
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 150 V Show Supplier Material materials with Comparative tracking index of 150 V | IEC 60112 |
Dielectric constant | 23.0 °C | 4.2 [-] Show Supplier Material materials with Dielectric constant of 4.2 [-] | IEC 60250 |
Dielectric strength | 23.0 °C | 16 kV/mm Show Supplier Material materials with Dielectric strength of 16 kV/mm | IEC 60243 |
Dissipation factor | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Dissipation factor of 2E-3 [-] | IEC 60250 |
Volume resistivity | 23.0 °C | 2.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 2.00E+15 Ω·cm | IEC 60093 |
Technological properties
Property | ||
---|---|---|
Application areas | In the electronics industry for the production of connectors, wiring device, frequency divider and a variety of instrument components, such as shell; in the aerospace industry for the production of high strength, high temperature resistant and insulation of the high performance requirements of thin-walled parts; in the chemical industry for the production of corrosion-resistant valves, insulation devices in military products, for the production of precision electrical connectors, high strength, high temperature resistant contactor shell, motor module, pump impeller, pump, chemical pump etc. | |
Fillers | 40% Glass Fiber | |
Processing methods | Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min |