Lead Glass SCHOTT 8652

Alternative and trade names
SCHOTT 8652
Want to keep this datasheet? Save it now in your required format

Description

Tungsten sealing glass. Low melting passivation glass wit high hydrolytic resistance.

Ashby charts

See where Lead Glass SCHOTT 8652 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

3.18 g/cm³ at 20 °C

Mechanical

Elastic modulus

E

58 GPa at 20 °C

Show Lead Glass materials with Elastic modulus of 58 GPa at 20 °C

Poisson's ratio

ν

0.25 [-] at 20 °C

Show Lead Glass materials with Poisson's ratio of 0.25 [-] at 20 °C

Thermal

Annealing temperature

Tanneal

490 °C

Viscosity 10¹³ dPa.s (ISO 7884-4)

Coefficient of thermal expansion

α

4.5E-6 1/K at 20 °C

mean value for 20-300 °C - ISO 7991

Glass transition temperature

Tg

495 °C

ISO 7884-8

Softening temperature

Tsoftening

638 °C

Viscosity 10⁷·⁶ dPa.s (ISO 7884-3)

Thermal conductivity

λ

0.9 W/(m·K) at 90 °C

Working temperature

Tworking

900 °C

Viscosity 10⁴ dPa.s (ISO 7884-2)

Electrical

Dielectric constant, 1MHz

εr,1MHz

6.9 [-] at 20 °C

Loss tangent, 1MHz

tanδ1,MHz

3.5E-3 [-] at 20 °C

Optical

Refractive index

nd

1.59 [-]

at λ=587.6 nm

Stress optical coefficient

k

3.4E-6 mm²/N

DIN 52314

Technological properties

Application areas

For power and pin diodes as well as microdiodes, Signal intensifier, detector (other Electrotechnology/Electronics), Sensors

Corrosion properties

Hydrolytic resistance Class HGB1 (ISO 719) - Acid resistance Class S4 (DIN 12116) - Alkali resistance Class A3 (ISO695)

This material data has been provided by Schott Glass Tubing.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.