General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 20.0 °C | 0.68 g/cm³ Show Material materials with Density of 0.68 g/cm³ | |
Film yield | 20.0 °C | 31.29 - 42.02 m²/kg Show Material materials with Film yield of 31.29 - 42.02 m²/kg | |
Shrinkage | 120.0 °C | 4 % Show Material materials with Shrinkage of 4 % | GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min) |
Shrinkage, transverse | 120.0 °C | 2 % Show Material materials with Shrinkage, transverse of 2 % | GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min) |
Surface density | 20.0 °C | 2.38E-3 - 3.2E-3 g/cm² Show Material materials with Surface density of 2.38E-3 - 3.2E-3 g/cm² |
Dimension
| Property | Value |
|---|---|
Thickness | 0.04 - 0.05 mm Show Material materials with Thickness of 0.04 - 0.05 mm |
Dimensions | Available thicknesses: 35, 38, 47µm. |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongation | 20.0 °C | 200 % Show Material materials with Elongation of 200 % | GOST 14236, ISO 527, ASTM D882 |
Elongation, transverse | 20.0 °C | 70 % Show Material materials with Elongation, transverse of 70 % | GOST 14236, ISO 527, ASTM D882 |
Tensile strength | 20.0 °C | 80 MPa Show Material materials with Tensile strength of 80 MPa | GOST 14236, ISO 527, ASTM D882 |
Tensile strength, transverse | 20.0 °C | 150 MPa Show Material materials with Tensile strength, transverse of 150 MPa | GOST 14236, ISO 527, ASTM D882 |
Optical
| Property | Value | Comment |
|---|---|---|
Luminous transmittance | 20 - 30 [-] Show Material materials with Luminous transmittance of 20 - 30 [-] | GOST 15875, ISO 14782, ASTM D 1003 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | High quality solvent rotogravure and flexographic direct printing, for production of fully wrapped labels for bottles, for labeling with cold and hot melt glue. | |
| Friction | Kinetic coefficient of friction µ= 0.2-0.4 (GOST 27492, ISO 8295, ASTM D 1894). | |
| Other | LOBA BOPP films comprise: A modified copolymer corona treated skin layer, a white opaque oriented polypropylene tie layer, a white pearl cavitated core layer of oriented polypropylene, an oriented polypropylene tie layer, a glossy non-heat-sealable, non treated skin layer with standard coefficient of friction. | |
| Processing history | Treatment level: 38 mN/m (ISO 8296, ASTM D 2578). | |