HGHL BOPP (Biaxially Oriented Polypropylene) Transparent Film
Description
Heat sealable transparent BOPP film with low coefficient of friction and low heat sealing threshold for high-speed packaging machines. For high quality rotogravure and flexographic printing and lamination. The main advantages are: A wide range of heat sealing; contains slip-antistatic and antiblocking additives; excellent optical properties; good mechanical properties; intended for contact with food; both side low coefficient of friction; without coatings and primers.
Properties
Dimension
Thickness t
0.02 - 0.05 mm
General
Density ρ
0.91 g/cm³ at 20 °C
Film yield Yfilm
22.89 - 73.26 m²/kg at 20 °C
Shrinkage cshrink
4 - 5 % at 120 °C
GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min)
Shrinkage, transverse cshrink, trans
2 - 3 % at 120 °C
GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min)
Surface density ρsurf
1.365E-3 - 4.368E-3 g/cm² at 20 °C
Material Information
Dimension
Available thicknesses: 15, 18, 20, 25, 30, 35, 40, 48µm.
Mechanical
Elongation A
200 - 220 % at 20 °C
GOST 14236, ISO 527, ASTM D882
Elongation, transverse A
70 - 80 % at 20 °C
GOST 14236, ISO 527, ASTM D882
Tensile strength Rm
130 - 140 MPa at 20 °C
GOST 14236, ISO 527, ASTM D882
Tensile strength, transverse Rm,trans
230 - 250 MPa at 20 °C
GOST 14236, ISO 527, ASTM D882
Optical
Haze H
2.5 - 3.2 %
GOST 15875, ISO 14782, ASTM D 1003
Technological properties
Application areas
High quality solvent based rotogravure and flexographic printing; solvent based and solvent free lamination with polyurethane adhesives; manufacture of flexible packaging for food products; for high-speed vertical VFFS and horizontal HFFS packaging machines.
Friction
Kinetic coefficient of friction µ= 0.1-0.25 (GOST 27492, ISO 8295, ASTM D 1894).
Other
HGHL BOPP films comprise: A treated modified heat sealable copolymer skin layer, a transparent oriented polypropylene core layer, a heat sealable, non treated skin layer with low seal intention temperature and low coefficient of friction.
Processing history
Treatment level: 38 mN/m (ISO 8296, ASTM D 2578).
This material data has been provided by SIBUR.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.
Materials by this supplier
HGSL BOPP (Biaxially Oriented Polypropylene) Transparent Film
HGPL BOPP (Biaxially Oriented Polypropylene) Transparent Film
HGHW BOPP (Biaxially Oriented Polypropylene) Transparent Film
HGFL BOPP (Biaxially Oriented Polypropylene) Transparent Film
HASL BOPP (Biaxially Oriented Polypropylene) Transparent Film