General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 20.0 °C | 0.91 g/cm³ Show Material materials with Density of 0.91 g/cm³ | |
Film yield | 20.0 °C | 31.4 - 73.26 m²/kg Show Material materials with Film yield of 31.4 - 73.26 m²/kg | |
Shrinkage | 120.0 °C | 4 - 5 % Show Material materials with Shrinkage of 4 - 5 % | GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min) |
Shrinkage, transverse | 120.0 °C | 2 % Show Material materials with Shrinkage, transverse of 2 % | GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min) |
Surface density | 20.0 °C | 1.36E-3 - 3.18E-3 g/cm² Show Material materials with Surface density of 1.36E-3 - 3.18E-3 g/cm² |
Dimension
Property | Value |
---|---|
Thickness | 0.02 - 0.04 mm Show Material materials with Thickness of 0.02 - 0.04 mm |
Dimensions | Available thicknesses: 15, 20, 25, 30, 35µm. |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 20.0 °C | 200 % Show Material materials with Elongation of 200 % | GOST 14236, ISO 527, ASTM D882 |
Elongation, transverse | 20.0 °C | 70 % Show Material materials with Elongation, transverse of 70 % | GOST 14236, ISO 527, ASTM D882 |
Tensile strength | 20.0 °C | 140 - 150 MPa Show Material materials with Tensile strength of 140 - 150 MPa | GOST 14236, ISO 527, ASTM D882 |
Tensile strength, transverse | 20.0 °C | 250 MPa Show Material materials with Tensile strength, transverse of 250 MPa | GOST 14236, ISO 527, ASTM D882 |
Optical
Property | Value | Comment |
---|---|---|
Haze | 2 % Show Material materials with Haze of 2 % | GOST 15875, ISO 14782, ASTM D 1003 |
Technological properties
Property | ||
---|---|---|
Application areas | High quality rotogravure and flexographic solvent printing; solvent or solventless polyurethane laminating adhesives; for the production of flexible packaging (typically duplex) with frame cold seal glue. | |
Friction | Kinetic coefficient of friction µ= 0.1-0.35 (GOST 27492, ISO 8295, ASTM D 1894). | |
Other | PGR BOPP films comprise: A treated modified copolymer skin layer, a transparent oriented polypropylene core layer, a non-heat-sealable, untreated release skin layer with low coefficient of friction. | |
Processing history | Treatment level: 38 mN/m (ISO 8296, ASTM D 2578). |