Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 20.0 °C | 2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | T73 | WL 3.4364-1, DIN 1725-1 | Forging, Profile |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bulk Modulus | 20.0 °C | 72.5 GPa Show Material materials with Bulk Modulus of 72.5 GPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging, Profile | |
Elastic modulus | 20.0 °C | 71.0 GPa Show Material materials with Elastic modulus of 71.0 GPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging, Profile | |
Elongation | 20.0 °C | 2.0 % Show Material materials with Elongation of 2.0 % | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse |
20.0 °C | 3.0 % Show Material materials with Elongation of 3.0 % | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse | |
20.0 °C | 4.0 % Show Material materials with Elongation of 4.0 % | T73 | WL 3.4364-1, DIN 1725-1 | Profile, Forging | Transverse | |
20.0 °C | 5.0 % Show Material materials with Elongation of 5.0 % | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse | |
20.0 °C | 6.0 % Show Material materials with Elongation of 6.0 % | T73 | WL 3.4364-1, DIN 1725-1 | Profile, Forging | ||
20.0 °C | 7.0 % Show Material materials with Elongation of 7.0 % | T73 | WL 3.4364-1, DIN 1725-1 | Forging | ||
20.0 °C | 8.0 % Show Material materials with Elongation of 8.0 % | T73 | WL 3.4364-1, DIN 1725-1 | Profile | ||
Hardness, Brinell | 20.0 °C | 130.0 [-] Show Material materials with Hardness, Brinell of 130.0 [-] | T73 | WL 3.4364-1, DIN 1725-1 | Profile | Transverse |
20.0 °C | 130.0 [-] Show Material materials with Hardness, Brinell of 130.0 [-] | T73 | WL 3.4364-1, DIN 1725-1 | Profile | ||
20.0 °C | 135.0 [-] Show Material materials with Hardness, Brinell of 135.0 [-] | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse | |
20.0 °C | 135.0 [-] Show Material materials with Hardness, Brinell of 135.0 [-] | T73 | WL 3.4364-1, DIN 1725-1 | Forging | ||
20.0 °C | 150.0 [-] Show Material materials with Hardness, Brinell of 150.0 [-] | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse | |
Plane-Strain Fracture Toughnes | 20.0 °C | 24.6 - 40.1 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.6 - 40.1 MPa·√m | T73 | WL 3.4364-1, DIN 1725-1 | Forging | |
20.0 °C | 24.6 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.6 MPa·√m | T73 | WL 3.4364-1, DIN 1725-1 | Forging | ||
20.0 °C | 24.6 - 24.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.6 - 24.9 MPa·√m | T73 | WL 3.4364-1, DIN 1725-1 | Forging | ||
20.0 °C | 24.9 - 40.1 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.9 - 40.1 MPa·√m | T73 | WL 3.4364-1, DIN 1725-1 | Forging | ||
20.0 °C | 24.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.9 MPa·√m | T73 | WL 3.4364-1, DIN 1725-1 | Forging | ||
20.0 °C | 40.1 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 40.1 MPa·√m | T73 | WL 3.4364-1, DIN 1725-1 | Forging | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||||
Shear modulus | 26.4 - 27.1 GPa Show Material materials with Shear modulus of 26.4 - 27.1 GPa | Typical for Wrought 7000 Series Aluminium | ||||
Tensile strength | 20.0 °C | 390.0 MPa Show Material materials with Tensile strength of 390.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse |
20.0 °C | 400.0 MPa Show Material materials with Tensile strength of 400.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse | |
20.0 °C | 405.0 MPa Show Material materials with Tensile strength of 405.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse | |
20.0 °C | 415.0 MPa Show Material materials with Tensile strength of 415.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse | |
20.0 °C | 420.0 MPa Show Material materials with Tensile strength of 420.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse | |
20.0 °C | 420.0 MPa Show Material materials with Tensile strength of 420.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging | ||
20.0 °C | 425.0 MPa Show Material materials with Tensile strength of 425.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse | |
20.0 °C | 425.0 MPa Show Material materials with Tensile strength of 425.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging | ||
20.0 °C | 435.0 MPa Show Material materials with Tensile strength of 435.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse | |
20.0 °C | 440.0 MPa Show Material materials with Tensile strength of 440.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse | |
20.0 °C | 440.0 MPa Show Material materials with Tensile strength of 440.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging | ||
20.0 °C | 450.0 MPa Show Material materials with Tensile strength of 450.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Profile | Transverse | |
20.0 °C | 450.0 MPa Show Material materials with Tensile strength of 450.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Profile | ||
20.0 °C | 455.0 MPa Show Material materials with Tensile strength of 455.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging | ||
20.0 °C | 480.0 MPa Show Material materials with Tensile strength of 480.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse | |
20.0 °C | 480.0 MPa Show Material materials with Tensile strength of 480.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Profile | ||
20.0 °C | 490.0 MPa Show Material materials with Tensile strength of 490.0 MPa | T73 | WL 3.4364-1, DIN 1725-1 | Forging | Transverse |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.1e-05 - 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1e-05 - 2.4e-05 1/K | Typical for Wrought 7000 Series Aluminium |
Melting point | 465.0 - 655.0 °C Show Material materials with Melting point of 465.0 - 655.0 °C | Typical for Wrought 7000 Series Aluminium |
Specific heat capacity | 795.0 - 1050.0 J/(kg·K) Show Material materials with Specific heat capacity of 795.0 - 1050.0 J/(kg·K) | Typical for Wrought 7000 Series Aluminium |
Thermal conductivity | 121.0 - 170.0 W/(m·K) Show Material materials with Thermal conductivity of 121.0 - 170.0 W/(m·K) | Typical for Wrought 7000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 34000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 34000000.0 S/m | Typical for Wrought 7000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5.6e-08 Ω·m Show Material materials with Electrical resistivity of 2.9e-08 - 5.6e-08 Ω·m | Typical for Wrought 7000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.18 - 0.28 % Show Material materials with Chromium of 0.18 - 0.28 % | T73 | WL 3.4364-1, DIN 1725-1 | Forging, Profile |
Copper | 1.2 - 2.0 % Show Material materials with Copper of 1.2 - 2.0 % | T73 | WL 3.4364-1, DIN 1725-1 | Forging, Profile |
Iron | 0.5 Show Material materials with Iron of 0.5 | T73 | WL 3.4364-1, DIN 1725-1 | Forging, Profile |
Magnesium | 2.1 - 2.9 % Show Material materials with Magnesium of 2.1 - 2.9 % | T73 | WL 3.4364-1, DIN 1725-1 | Forging, Profile |
Manganese | 0.3 Show Material materials with Manganese of 0.3 | T73 | WL 3.4364-1, DIN 1725-1 | Forging, Profile |
Silicon | 0.4 Show Material materials with Silicon of 0.4 | T73 | WL 3.4364-1, DIN 1725-1 | Forging, Profile |
Titanium | 0.2 Show Material materials with Titanium of 0.2 | T73 | WL 3.4364-1, DIN 1725-1 | Forging, Profile |
Zinc | 5.1 - 6.1 % Show Material materials with Zinc of 5.1 - 6.1 % | T73 | WL 3.4364-1, DIN 1725-1 | Forging, Profile |
Technological properties
| Property | ||
|---|---|---|
| Brazing | Excellent | |