EN 573-3 Grade AW-5019 H16

Want to keep this datasheet? Save it now in your required format

Description

Naturally hard AlMg alloy. The alloy is food safe.

Related Standards

Equivalent Materials

Ashby charts

See where EN 573-3 Grade AW-5019 H16 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.64 g/cm³ at 20 °C

Dimension

Dimensions

Wanddicke

Mechanical

Elastic modulus

E

70 GPa at 20 °C

Show 5000 Series materials with Elastic modulus of 70 GPa at 20 °C

Elongation

A

2 % at 20 °C

Show 5000 Series materials with Elongation of 2 % at 20 °C

Elongation A100

A100

2 % at 20 °C

Show 5000 Series materials with Elongation A100 of 2 % at 20 °C

Elongation A50

A50

2 % at 20 °C

Show 5000 Series materials with Elongation A50 of 2 % at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 5000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 5000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Typical for Wrought 5000 Series Aluminium

Shear modulus

G

27 GPa at 20 °C

Show 5000 Series materials with Shear modulus of 27 GPa at 20 °C

Tensile strength

Rm

320 MPa at 20 °C

Show 5000 Series materials with Tensile strength of 320 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

260 MPa at 20 °C

Show 5000 Series materials with Yield strength Rp0.2 of 260 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.25E-5 1/K at -50 °C

Hide chart

Max service temperature

Tmax

150 °C

Typical for Wrought 5000 Series Aluminium

Melting point

Tm

575 - 630 °C

Specific heat capacity

cp

904 J/(kg·K) at 20 °C

Thermal conductivity

λ

110 - 140 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

1.50E+7 - 1.90E+7 S/m at 20 °C

Electrical resistivity

ρel

5.26E-8 - 6.67E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Other

-

Mn + Cr = 0.1 - 0.6, each 0.05, total 0.15, Rest Al

Mg

4.5 - 5.6 %

Fe

0.5 %

Si

0.4 %

Cr

0.2 %

More

Technological properties

Anodizing

decorative: sufficient, Protective: very good

Brazing

hard brazing (with flux/ without flux): poor / poor, friction soldering: acceptable, soft brazing with flux: poor

Corrosion properties

Seawater: very good, weathering: very good

Workability

Bending / Spinning (cold): good / sufficient, Impact extrusion (cold): poor, Deep drawing / upsetting (Condition) good (O) / good (O)

This material data has been provided by WIAM,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.