General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 20.0 °C | 4.54 g/cm³ Show Material materials with Density of 4.54 g/cm³ | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 116.0 GPa Show Material materials with Elastic modulus of 116.0 GPa | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat | |
200.0 °C | 108.0 GPa Show Material materials with Elastic modulus of 108.0 GPa | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat | ||
400.0 °C | 99.0 GPa Show Material materials with Elastic modulus of 99.0 GPa | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat | ||
Elongation | 20.0 °C | 6.0 % Show Material materials with Elongation of 6.0 % | Annealed | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Plate | |
20.0 °C | 7.0 % Show Material materials with Elongation of 7.0 % | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod | Transverse | |
20.0 °C | 8.0 % Show Material materials with Elongation of 8.0 % | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate | ||
Hardness, Brinell | 20.0 °C | 320.0 Show Material materials with Hardness, Brinell of 320.0 | Annealed | DIN 17862, WL 3.7174-1, DIN 17851, DIN 17864, DIN 17860 | Rod | |
Plane-Strain Fracture Toughnes | 20.0 °C | 46.1 - 54.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 46.1 - 54.8 MPa·√m | Annealed | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Plate | |
20.0 °C | 46.1 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 46.1 MPa·√m | Annealed | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Plate | ||
20.0 °C | 54.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 54.8 MPa·√m | Annealed | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Plate | ||
20.0 °C | 62.7 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 62.7 MPa·√m | Annealed | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging | ||
20.0 °C | 62.7 - 71.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 62.7 - 71.9 MPa·√m | Annealed | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging | ||
20.0 °C | 62.7 - 70.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 62.7 - 70.8 MPa·√m | Annealed | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging | ||
20.0 °C | 70.8 - 71.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 70.8 - 71.9 MPa·√m | Annealed | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging | ||
20.0 °C | 70.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 70.8 MPa·√m | Annealed | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging | ||
20.0 °C | 71.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 71.9 MPa·√m | Annealed | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging | ||
Reduction of area | 20.0 °C | 15.0 % Show Material materials with Reduction of area of 15.0 % | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging | Transverse |
20.0 °C | 20.0 % Show Material materials with Reduction of area of 20.0 % | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate | ||
Shear modulus | 20.0 °C | 45.0 GPa Show Material materials with Shear modulus of 45.0 GPa | Annealed | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Forging, Plate, Rod, Flat | |
Tensile strength | 20.0 °C | 1000.0 MPa Show Material materials with Tensile strength of 1000.0 MPa | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod | Transverse |
20.0 °C | 1000.0 MPa Show Material materials with Tensile strength of 1000.0 MPa | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate | ||
20.0 °C | 1030.0 MPa Show Material materials with Tensile strength of 1030.0 MPa | Annealed | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Plate | ||
20.0 °C | 1070.0 MPa Show Material materials with Tensile strength of 1070.0 MPa | Annealed | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Flat | ||
20.0 °C | 1140.0 MPa Show Material materials with Tensile strength of 1140.0 MPa | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | |||
100.0 °C | 1065.0 MPa Show Material materials with Tensile strength of 1065.0 MPa | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | |||
200.0 °C | 990.0 MPa Show Material materials with Tensile strength of 990.0 MPa | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | |||
300.0 °C | 930.0 MPa Show Material materials with Tensile strength of 930.0 MPa | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | |||
400.0 °C | 900.0 MPa Show Material materials with Tensile strength of 900.0 MPa | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | 7.699999999999999e-06 - 1e-05 1/K Show Material materials with Coefficient of thermal expansion of 7.699999999999999e-06 - 1e-05 1/K | Typical for Titanium Alpha Beta Alloy | ||||
Melting point | 1500.0 - 1750.0 °C Show Material materials with Melting point of 1500.0 - 1750.0 °C | Typical for Titanium Alpha Beta Alloy | ||||
Specific heat capacity | 370.0 - 674.0 J/(kg·K) Show Material materials with Specific heat capacity of 370.0 - 674.0 J/(kg·K) | Typical for Titanium Alpha Beta Alloy | ||||
Thermal conductivity | 20.0 °C | 6.5 W/(m·K) Show Material materials with Thermal conductivity of 6.5 W/(m·K) | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical resistivity | 20.0 °C | 1.57e-06 Ω·m Show Material materials with Electrical resistivity of 1.57e-06 Ω·m | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminium | 5.0 - 6.0 % Show Material materials with Aluminium of 5.0 - 6.0 % | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat |
Carbon | 0.05 Show Material materials with Carbon of 0.05 | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat |
Copper | 0.35 - 1.0 % Show Material materials with Copper of 0.35 - 1.0 % | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat |
Hydrogen | 0.015 Show Material materials with Hydrogen of 0.015 | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod |
Iron | 0.35 - 1.0 % Show Material materials with Iron of 0.35 - 1.0 % | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat |
Nitrogen | 0.04 Show Material materials with Nitrogen of 0.04 | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat |
Oxygen | 0.2 Show Material materials with Oxygen of 0.2 | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat |
Tin | 1.5 - 2.5 % Show Material materials with Tin of 1.5 - 2.5 % | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat |
Titanium | 82.8 % Show Material materials with Titanium of 82.8 % | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat |
Vanadium | 5.0 - 6.0 % Show Material materials with Vanadium of 5.0 - 6.0 % | Annealed | DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860 | Forging, Rod, Plate, Flat |