EN 683-2 Grade AW-1200 H14

Want to keep this datasheet? Save it now in your required format

Description

Very good corrosion resistance and workability. Very ductile in annealed condition.

Related Standards

Equivalent Materials

Ashby charts

See where EN 683-2 Grade AW-1200 H14 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.69 - 2.72 g/cm³ at 20 °C

Dimension

Dimensions

Dicke

Thickness

t

60 - 400 mm

Mechanical

Bending angle 180°

θ180

1 - 1.5 °/t at 20 °C

Show 1000 Series materials with Bending angle 180° of 1 - 1.5 °/t at 20 °C

Bending angle 90°

θ90

0 - 2.5 °/t at 20 °C

Show 1000 Series materials with Bending angle 90° of 0 - 2.5 °/t at 20 °C

Elastic modulus

E

60 - 70 GPa at 20 °C

Show 1000 Series materials with Elastic modulus of 60 - 70 GPa at 20 °C

Elongation

A

5 - 6 % at 20 °C

Show 1000 Series materials with Elongation of 5 - 6 % at 20 °C

Elongation A100

A100

1 - 6 % at 20 °C

Show 1000 Series materials with Elongation A100 of 1 - 6 % at 20 °C

Elongation A50

A50

1 - 6 % at 20 °C

Show 1000 Series materials with Elongation A50 of 1 - 6 % at 20 °C

Elongation A50, transverse

A50,trans

1 - 6 % at 20 °C

Show 1000 Series materials with Elongation A50, transverse of 1 - 6 % at 20 °C

Elongation, transverse

A

6 % at 20 °C

Show 1000 Series materials with Elongation, transverse of 6 % at 20 °C

Hardness, Brinell

HB

30 - 37 [-] at 20 °C

Show 1000 Series materials with Hardness, Brinell of 30 - 37 [-] at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 1000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 1000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 1000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Shear modulus

G

24 - 26.5 GPa at 20 °C

Show 1000 Series materials with Shear modulus of 24 - 26.5 GPa at 20 °C

Tensile strength

Rm

105 - 170 MPa at 20 °C

Show 1000 Series materials with Tensile strength of 105 - 170 MPa at 20 °C

Tensile strength, transverse

Rm,trans

105 - 155 MPa at 20 °C

Show 1000 Series materials with Tensile strength, transverse of 105 - 155 MPa at 20 °C

Yield strength

YS

95 - 150 MPa at 20 °C

Show 1000 Series materials with Yield strength of 95 - 150 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

80 - 100 MPa at 20 °C

Show 1000 Series materials with Yield strength Rp0.2 of 80 - 100 MPa at 20 °C

Yield strength Rp0.2, transverse

Rp0.2,trans

90 - 95 MPa at 20 °C

Show 1000 Series materials with Yield strength Rp0.2, transverse of 90 - 95 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.17E-5 1/K at -50 °C

20-100°C

Hide chart

Melting point

Tm

644 - 657 °C

Specific heat capacity

cp

898 - 1004 J/(kg·K) at 20 °C

Thermal conductivity

λ

138 - 225 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

3.30E+7 - 3.55E+7 S/m at 20 °C

Electrical resistivity

ρel

2.94E-8 - 4.9E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Al

99 %

Fe

1 %

Si + Fe

Si

1 %

Si + Fe

Other

0.15 %

Si + Fe < 1.00, each 0.05, total 0.15

Zn

0.1 %

More

Technological properties

Anodizing

Very Good

Application areas

Facades: Single sheet, Sheets for composites/ sandwich Panels; Roofing: Foil for bituminous coating; Doors: Sheets for composites/ sandwich Panels; Electronic devices: Housing of devices; Heat exchangers: Fins; Cable wrapping: Electric cable wrapping; Insulation; Solar: Solar collectors; Semi-rigid and corrugated: Smooth wall

Brazing

Excellent

Corrosion properties

Very Good

Welding

Excellent

Workability

Excellent

This material data has been provided by Aludium,WIAM,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.