General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 6.05 g/cm³ Show Supplier Material materials with Density of 6.05 g/cm³ | |
Surface roughness | 0.6 μm Show Supplier Material materials with Surface roughness of 0.6 μm | Ra |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Compressive strength | 23.0 °C | 2300 MPa Show Supplier Material materials with Compressive strength of 2300 MPa | |
Elastic modulus | 23.0 °C | 205 GPa Show Supplier Material materials with Elastic modulus of 205 GPa | |
Flexural strength | 23.0 °C | 930 MPa Show Supplier Material materials with Flexural strength of 930 MPa | 4-point bending flexural test |
Hardness, Vickers | 23.0 °C | 1530 [-] Show Supplier Material materials with Hardness, Vickers of 1530 [-] | converted from GPa |
Plane-Strain Fracture Toughnes | 23.0 °C | 10 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 10 MPa·√m |
Thermal
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 20.0 °C | 1.00E+10 Ω·m Show Supplier Material materials with Electrical resistivity of 1.00E+10 Ω·m |
600.0 °C | 10000 Ω·m Show Supplier Material materials with Electrical resistivity of 10000 Ω·m | |
Technological properties
Property | ||
---|---|---|
Application areas | Sensor Technology (lambda sensors) for oxygen ion conduction Components that face frequent temperature changes, e.g. draw dies and high-temperature insulating parts In cases where high fracture toughness is required, e.g. for medical instruments | |
Processing history | Additive Manufactureing (AM) |