Allgemein
Property | Value | Condition | Related Standards |
---|---|---|---|
Dichte | 2.69 g/cm³ Show Material materials with Dichte of 2.69 g/cm³ | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Mechanisch
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Bending Fatigue Strength | 90.0 MPa Show Material materials with Bending Fatigue Strength of 90.0 MPa | H34 | AA Standards | |
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | |
Härte, Brinell | 53.0 [-] Show Material materials with Härte, Brinell of 53.0 [-] | H34 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Zugfestigkeit | 170.0 - 215.0 MPa Show Material materials with Zugfestigkeit of 170.0 - 215.0 MPa | H34 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
170.0 MPa Show Material materials with Zugfestigkeit of 170.0 MPa | H34 | AA Standards, ASTM B210, ASTM B483 | ||
190.0 MPa Show Material materials with Zugfestigkeit of 190.0 MPa | H34 | AA Standards |
Thermisch
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 2.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.38e-05 1/K | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | |
100 °C | 2.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.38e-05 1/K | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Schmelzpunkt | 625.0 - 650.0 °C Show Material materials with Schmelzpunkt of 625.0 - 650.0 °C | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Spezifische Wärmekapazität | 879.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Wärmeleitfähigkeit | 193 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 193 W/(m·K) | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Elektrisch
Property | Value | Condition | Related Standards |
---|---|---|---|
Elektrische Leitfähigkeit | 29000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 29000000.0 S/m | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
spezifischer Widerstand | 3.45e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.45e-08 Ω·m | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Chrom | 0.1 % Show Material materials with Chrom of 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Eisen | 0.70 % Show Material materials with Eisen of 0.70 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Kupfer | 0.2 % Show Material materials with Kupfer of 0.2 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Magnesium | 1.1 - 1.8 % Show Material materials with Magnesium of 1.1 - 1.8 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Mangan | 0.1 % Show Material materials with Mangan of 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Silizium | 0.4 % Show Material materials with Silizium of 0.4 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Technological properties
Property | ||
---|---|---|
Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: not suitable (O), poor (H32, H34), sufficient (H36, H38) | |
Workability | general (condition): good (O, H32), acceptable (H34), poor(H36, H38) |