Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.64 g/cm³ Show Material materials with Dichte of 2.64 g/cm³ | O | AA Standards, ASTM B211, ASTM B316 |
Mechanisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 140.0 MPa Show Material materials with Bending Fatigue Strength of 140.0 MPa | O | AA Standards | |
Elastizitätsmodul | 71.0 GPa Show Material materials with Elastizitätsmodul of 71.0 GPa | O | AA Standards, ASTM B211, ASTM B316 | |
Härte, Brinell | 65.0 [-] Show Material materials with Härte, Brinell of 65.0 [-] | O | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Zugfestigkeit | 290.0 MPa Show Material materials with Zugfestigkeit of 290.0 MPa | O | AA Standards | |
320.0 MPa Show Material materials with Zugfestigkeit of 320.0 MPa | O | AA Standards, ASTM B211, ASTM B316 |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 20 °C | 2.41e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.41e-05 1/K | O | AA Standards, ASTM B211, ASTM B316 | |
100 °C | 2.41e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.41e-05 1/K | O | AA Standards, ASTM B211, ASTM B316 | ||
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Schmelzpunkt | 565.0 - 640.0 °C Show Material materials with Schmelzpunkt of 565.0 - 640.0 °C | O | AA Standards, ASTM B211, ASTM B316 | ||
Spezifische Wärmekapazität | 879.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Wärmeleitfähigkeit | 109.0 - 117.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 109.0 - 117.0 W/(m·K) | O | AA Standards, ASTM B211, ASTM B316 |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 16000000.0 - 17000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 16000000.0 - 17000000.0 S/m | O | AA Standards, ASTM B211, ASTM B316 |
spezifischer Widerstand | 5.88e-08 - 6.25e-08 Ω·m Show Material materials with spezifischer Widerstand of 5.88e-08 - 6.25e-08 Ω·m | O | AA Standards, ASTM B211, ASTM B316 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chrom | 0.05 - 0.2 % Show Material materials with Chrom of 0.05 - 0.2 % | O | AA Standards, ASTM B211, ASTM B316 |
Eisen | 0.40 % Show Material materials with Eisen of 0.40 % | O | AA Standards, ASTM B211, ASTM B316 |
Kupfer | 0.1 % Show Material materials with Kupfer of 0.1 % | O | AA Standards, ASTM B211, ASTM B316 |
Magnesium | 4.5 - 5.6 % Show Material materials with Magnesium of 4.5 - 5.6 % | O | AA Standards, ASTM B211, ASTM B316 |
Mangan | 0.05 - 0.2 % Show Material materials with Mangan of 0.05 - 0.2 % | O | AA Standards, ASTM B211, ASTM B316 |
Silizium | 0.3 % Show Material materials with Silizium of 0.3 % | O | AA Standards, ASTM B211, ASTM B316 |
Zink | 0.1 % Show Material materials with Zink of 0.1 % | O | AA Standards, ASTM B211, ASTM B316 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (O, H111, H12, H32, H14, H34), c (H18, H38), d (H192, H392), general: sehr gut, ohne Schutz in industrieller oder Seewasser-Atmosphäre (O, H111, H12, H32, H14, H34, H18, H38), b (H192, H392) | |
| General machinability | General: poor (O, H111, H12, H32), sufficient (H14, H34, H18, H38), good to acceptable (H192, H392) | |
| Workability | general (condition): good (O, H111), acceptable (H12, H32, H14, H34), poor(H18, H38), d (H192, H392) | |